PolyOne FireCon™ CPE 1240 UV RoHS NATURAL Polyethylene, Chlorinated (CPE)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	PolyOne Corporation
Trade Name	FireCon™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne FireCon™ CPE 1240 UV RoHS NATURAL Polyethylene, Chlorinated (CPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

An excellent choice for low-voltage power-and-cable control cables, this RoHS compliant filled, flexible thermoplastic CPE jacketing compound offers wire and cable manufacturers the advantages of thermoplastic extrusion processing without the need to invest in continuous vulcanization (CV) equipment. CPE 1240 UV RoHS Natural is excellent for larger-diameter cable. This compound passes testing for heat/shock resistance, which requires cable to withstand being bent and twisted without cracking or showing stress. Good moisture, oil, and electrical properties. Applications include power-and-control cable for fossil-fuel and co-generation plants.Note: Natural - Typical processing temperatures range between 290°-330°F depending upon screw design. Contact Technical Service for recommendation for specific equipment. Note: Pre-drying is recommended for 4 hours at 175°-185°F. NOTE: Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.32 g/cc	1.32 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	48	48	10 sec; ASTM D2240
Tensile Strength at Break	16.5 MPa	2390 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	500 %	500 %	Type IV, 510 mm/min; ASTM D638
Tensile Modulus	0.00896 GPa	1.30 ksi	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Oxygen Index	33 % @Thickness 1.91 mm	33 % @Thickness 0.0752 in	ASTM D2863

Descriptive Properties	Value	Comments
Additive	UV Stabilizer
Appearance	Pellets/Cubes	ASTM D2090
Change in Tensile Strain at Break	88%	IEC 60811-2-1; 70°C, 24 hr, in IRM 902 Oil
Change in Tensile Stress	60%	IEC 60811-2-1; 70°C, 24 hr, in IRM 902 Oil
Features	Flame Retardant
Forms	Pellets
Generic Material	CPE
Generic Name	Polyethylene, Chlorinated (CPE)
Processing Method	Extrusion
Regional Availability	Asia Pacific
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Cable Jacketing
	Wire & Cable Applications