PolyOne FireCon™ CPE 0883-01 RoHS BLACK Polyethylene, Chlorinated (CPE)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	PolyOne Corporation
Trade Name	FireCon™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne FireCon™ CPE 0883-01 RoHS BLACK Polyethylene, Chlorinated (CPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CPE-0833-1 RoHS BLACK is a heavy duty thermoplastic jacket for power and control cables. It is suitable for VW1 and tray fire rated applications. CPE-0833-1 RoHS BLACK offers the highest level of fire retardance which may be of benefit for concentric neutral applications.Note: Pre-drying is recommended for 4 hours at 175°-185°F. Note: Typical processing temperatures range between 320°-390°F depending upon screw design. Contact Technical Service for recommendation for specific equipment. NOTE: Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.37 g/cc	1.37 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	38	38	10 sec; ASTM D2240
Tensile Strength at Break	13.1 MPa	1900 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	450 %	450 %	Type IV, 510 mm/min; ASTM D638
Tensile Modulus	0.00586 GPa	0.850 ksi	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Oxygen Index	38 % @Thickness 1.91 mm	38 % @Thickness 0.0752 in	ASTM D2863

Descriptive Properties	Value	Comments
Appearance	Pellets/Cubes	ASTM D2090
Forms	Pellets
Generic Material	CPE
Generic Name	Polyethylene, Chlorinated (CPE)
Regional Availability	Asia Pacific
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Cable Jacketing
	Wire & Cable Applications