- PolyOne Edgetek® ES-06CF-09GF/000 RED Polyethersulfone - 6% Carbon - 9% Glass Fiber Reinforced - ESD Applications &
PolyOne Edgetek® ES-06CF-09GF/000 RED Polyethersulfone - 6% Carbon - 9% Glass Fiber Reinforced - ESD Applications &
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), Glass + Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ES-06CF-09GF/000 RED Polyethersulfone - 6% Carbon - 9% Glass Fiber Reinforced - ESD Applications
&.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 0.38 % | 0.38 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Tensile Strength, Ultimate | 117 MPa | 17000 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm @Thickness 6.35 mm |
0.899 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | IN HOUSE TEST V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10000 ohm-cm - 1e+05 | 10000 ohm-cm - 1e+05 | ASTM D257 |
| Surface Resistance | 1e+05 - 5.00e+7 ohm | 1e+05 - 5.00e+7 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 382 °C | 669 - 720 °F | Stock |
| Mold Temperature | 93.0 - 121 °C | 199 - 250 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F |
Users viewing this material also viewed the following:
- Lavergne VYTEEN ABS 2901 Acrylonitrile Butadiene Styrene
- Momentive Performance Materials Addisilâ„¢ 460 E Healthcare Extrusion Grade Heat Cured Rubber
- SABIC Innovative Plastics LNP LUBRILOY D20001 PPO
- SABIC Innovative Plastics LNP STAT-KON RX06001 PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL EXNL0353 PPE+HIPS
- Braskem IA58 HDPE Injection Molding Polyethylene Copolymer
- 3M Dyneon™ TFM™ 2001Z PTFE
- Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 350ºF Cure Temperature
Copyright © lookpolymers.com All Rights Reserved