PolyOne Edgetek® AM-10CF-20GF/000 HS Polyphthalamide (PPA), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AM-10CF-20GF/000 HS Polyphthalamide (PPA), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0035 - 0.0040 cm/cm | 0.0035 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 183 MPa | 26500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.4 GPa | 1650 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 11.4 GPa | 1650 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 277 °C | 530 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 510 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 - 1.00e+12 ohm-cm | 1e+05 - 1.00e+12 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1e+05 - 1.00e+12 ohm | 1e+05 - 1.00e+12 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 304 - 327 °C | 580 - 620 °F | Molding |
| Mold Temperature | >= 135 °C | >= 275 °F | |
| Drying Temperature | 110 - 121 °C | 230 - 250 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Oxford Polymers OPX782 Polybutylene Terephthalate (PBT), Impact Modified/ Glass Beads
- PolyOne Bergamid™ B700 UF V2 Polyamide 6 (Nylon 6)
- Fujipoly Industries FLAT-5TV-20-.75 silicone rubber fusible tape
- Lanxess Durethan® BKV 130 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified
- Lucite International Diakon® TD510 Toughened Acrylic Compound
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC (Asia Pacific)
- Solvay Specialty Polymers Veradel® 3500 Polyethersulfone (PESU)
- Westlake Elevate™ DA528AA Ethylene Vinyl Acetate Copolymer
- Arkema Group Rilsan® BMN D Nylon 11 (Dry)
- DuPont Performance Polymers Zytel® 101L NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved