Polimeri Europa Clearflex® FF 508 Octene Copolymer Linear Medium Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® FF 508 Octene Copolymer Linear Medium Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex FF 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films manufactured with Clearflex FF 508 are characterized by excellent optical properties, if compared to the resin density, high rigidity and temperature resistance, and optimum sealing properties.Main Applications: Due to its high optical, mechanical and sealing performances, Clearflex FF 508 is recommended for applications in which the high rigidity and the optimum gloss of this resin are a key factor (hygienic film, packaging for mineral water). The high Vicat softening point makes Clearflex FF 508 ideal for the production of film for food which is submitted to pasteurization or sterilization processes.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.934 g/cc
0.934 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 0.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 16.0 MPa
2320 psi
ISO 527-3
Film Tensile Strength at Yield, TD 18.0 MPa
2610 psi
ISO 527-3
Film Elongation at Break, MD 550 %
550 %
ISO 527-3
Film Elongation at Break, TD 750 %
750 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 3.5665 g/micron
90.589 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 20.38 g/micron
517.7 g/mil
ISO 6383-2
Dart Drop Test 90.0 g
0.198 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ISO 527-3
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ISO 527-3
1% Secant Modulus, MD 400 MPa
58000 psi
ISO 527-3
1% Secant Modulus, TD 450 MPa
65300 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 127 °C
261 °F
Internal method
Vicat Softening Point 117 °C

@Load 1.00 kg
243 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 12 %
12 %
ISO 14782
Gloss 60 %
60 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified