Plenco 6527 Phenolic, Granular, Injection Molded
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Resole, Mineral/Wood Filled |
| Manufacturer | Plenco (Plastics Engineering Company) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plenco 6527 Phenolic, Granular, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PLENCO 06527 is a woodflour and mineral filled resole phenolic molding compound.Information supplied by Plenco.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | ASTM D1895 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Water Absorption | 0.37 % | 0.37 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0046 cm/cm | 0.0046 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 48 | 48 | ASTM D785 |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 0.73 % | 0.73 % | ASTM D638 |
| Tensile Modulus | 10.7 GPa | 1550 ksi | ASTM D638 |
| Flexural Strength | 73.0 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM D790 |
| Compressive Strength | 127 MPa | 18400 psi | ASTM D695 |
| Izod Impact, Notched | 0.230 J/cm | 0.431 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.215 J/cm² | 1.02 ft-lb/in² | ASTM D256 |
| Impact | 173 | 173 | J/m Drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 188 °C | 370 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | ASTM D648 |
| Shrinkage | 0.31 % | 0.31 % | 72 hr, 120ºC; ASTM D1299 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.80e+12 ohm-cm | 1.80e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.6 | 6.6 | ASTM D150 |
| Dielectric Strength | 8.80 kV/mm | 224 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.083 | 0.083 | ASTM D150 |
| Arc Resistance | 153 sec | 153 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 123X PC Copolymer (Europe-Africa-Middle East)
- H.C. Starck Amperit® 512.074 Agglomerated Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- SABIC Innovative Plastics LNP THERMOCOMP DX11354X PC (Asia Pacific)
- Borealis Casico™ FR6083 Reduced Fire Hazard Jacketing Compound
- A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6
- ChevronTexaco Dura-Lith® NLGI 3 Grease EP
- Eurofoam Siliconcell SIL 411 Silicone Foam Sheet
- Dow Corning 1598 Performance Modifier
- Eastman Tenite Propionate 358A4000008 Clear, Trsp Cellulose Acetate Propionate
- Sinotek Materials ZSLG95 High Carbon Graphite
Copyright © lookpolymers.com All Rights Reserved