Plenco 51335 PET, Pellet, Injection Molded, Black (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Recycled, Glass Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plenco 51335 PET, Pellet, Injection Molded, Black (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PLENCO 51335 is an engineering grade glass reinforced recycled polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed and available in black only.Information supplied by PlencoPlenco discontinued their PET product line in 2005.

Physical Properties	Metric	English	Comments
Density	1.63 g/cc	0.0589 lb/in³	ASTM D792
Water Absorption	0.060 %	0.060 %	ASTM D570
Linear Mold Shrinkage	0.0015 cm/cm	0.0015 in/in	ATM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	21	21	ASTM D785
Tensile Strength, Ultimate	111.7 MPa	16200 psi	ASTM D638
Elongation at Break	1.36 %	1.36 %	ASTM D638
Tensile Modulus	9.29 GPa	1350 ksi	ASTM D638
Flexural Yield Strength	164.6 MPa	23870 psi	ASTM D790
Flexural Modulus	8.69 GPa	1260 ksi	ASTM D790
Compressive Yield Strength	168.9 MPa	24500 psi	ASTM D695
Izod Impact, Notched	0.490 J/cm	0.918 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	215 °C	419 °F	ASTM D648
Flammability, UL94	HB @Thickness 1.47 mm	HB @Thickness 0.0579 in

Electrical Properties	Metric	English	Comments
Electrical Resistivity	9.90e+15 ohm-cm	9.90e+15 ohm-cm	ASTM D257
Dielectric Constant	3.4 @Frequency 1e+6 Hz	3.4 @Frequency 1e+6 Hz	ASTM D150
Dielectric Strength	15.1 kV/mm	384 kV/in	Short Time; ASTM D149
Dissipation Factor	0.013 @Frequency 1e+6 Hz	0.013 @Frequency 1e+6 Hz	ASTM D150
Arc Resistance	30 sec	30 sec	ASTM D495
Comparative Tracking Index	225 V	225 V	ASTM D3638