Plenco 304 Black Impact Grade Woodflour/Cellulose Filled Phenolic Molding Compound (discontinued **)

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Impact Grade, Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plenco 304 Black Impact Grade Woodflour/Cellulose Filled Phenolic Molding Compound (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plaslok 304 is a two-stage, woodflour and cellulose-filled phenolic molding compound having improved impact strength. It is suitable for automatic molding, and is recommended for thin-walled parts or where mechanical assembly stress is experienced.Data provided by Plaslok Corporation.Plaslok Corporation was purchased by Plastics Engineering Company in March 2000. The Plaslok name is no longer used on any products.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ASTM D792
Apparent Bulk Density	0.500 g/cc	0.0181 lb/in³	ASTM D1895
Water Absorption	0.40 %	0.40 %	ASTM D570
Linear Mold Shrinkage	0.0080 cm/cm	0.0080 in/in	Compression; ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	52.0 MPa	7540 psi	ASTM D638
Flexural Yield Strength	76.0 MPa	11000 psi	ASTM D790
Flexural Modulus	8.30 GPa	1200 ksi	ASTM D790
Compressive Yield Strength	207 MPa	30000 psi	ASTM D695

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	166 °C	331 °F	ASTM D648

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	ASTM D257
Dielectric Constant	4.8 @Frequency 1e+6 Hz	4.8 @Frequency 1e+6 Hz	ASTM D150
	7.2 @Frequency 60 Hz	7.2 @Frequency 60 Hz	ASTM D150
Dielectric Strength	13.4 kV/mm	340 kV/in	ASTM D149
Dissipation Factor	0.040 @Frequency 1e+6 Hz	0.040 @Frequency 1e+6 Hz	ASTM D150
	0.14 @Frequency 60 Hz	0.14 @Frequency 60 Hz	ASTM D150

Users viewing this material also viewed the following: