PlastxWorld CEVIAN® S1100 High Impact PC/ABS alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer PlastxWorld, Inc.
Trade Name CEVIAN®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PlastxWorld CEVIAN® S1100 High Impact PC/ABS alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 7.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 7.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 53.1 MPa
7700 psi
ASTM 638
Elongation at Break 70 %
70 %
ASTM D638
Flexural Yield Strength 84.1 MPa
12200 psi
ASTM D790
Flexural Modulus 2.25 GPa
327 ksi
ASTM D790
Izod Impact, Notched 5.87 J/cm

@Thickness 6.35 mm
 11.0 ft-lb/in

@Thickness 0.250 in
 ASTM D256
6.41 J/cm

@Thickness 3.17 mm
 12.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
3.74 J/cm

@Thickness 6.35 mm,
Temperature -30.0 °C
 7.00 ft-lb/in

@Thickness 0.250 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
0.25 inch; ASTM D648
Vicat Softening Point 239 °C
462 °F
ASTM D1525
Flammability, UL94 HB
HB