Material Notes:
Physical Properties Metric English Comments
Density 1.21 - 1.34 g/cc
0.0437 - 0.0484 lb/in³
Average value: 1.29 g/cc Grade Count:8
Linear Mold Shrinkage 0.00830 - 0.0120 cm/cm
0.00830 - 0.0120 in/in
Average value: 0.00953 cm/cm Grade Count:3
Melt Flow 1.21 - 24.2 g/10 min
1.21 - 24.2 g/10 min
Average value: 9.36 g/10 min Grade Count:4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 58.6 - 92.2 MPa
8500 - 13400 psi
Average value: 80.9 MPa Grade Count:7
57.9 - 57.9 MPa

@Temperature 150 - 150 °C
 8400 - 8400 psi

@Temperature 302 - 302 °F
 Average value: 57.9 MPa Grade Count:1
Tensile Strength, Yield 57.916 - 57.916 MPa

@Temperature 149 - 149 °C
 8400.0 - 8400.0 psi

@Temperature 300 - 300 °F
 Average value: 57.9 MPa Grade Count:1
Elongation at Break 1.80 - 90.0 %
1.80 - 90.0 %
Average value: 17.0 % Grade Count:7
90.0 - 90.0 %

@Temperature 150 - 150 °C
 90.0 - 90.0 %

@Temperature 302 - 302 °F
 Average value: 90.0 % Grade Count:1
Elongation at Yield 90.0 - 90.0 %

@Temperature 149 - 149 °C
 90.0 - 90.0 %

@Temperature 300 - 300 °F
 Average value: 90.0 % Grade Count:1
Modulus of Elasticity 2.41 - 4.50 GPa
350 - 653 ksi
Average value: 3.73 GPa Grade Count:7
Flexural Yield Strength 77.2 - 137 MPa
11200 - 19900 psi
Average value: 110 MPa Grade Count:5
88.2529 - 88.3 MPa

@Temperature 149 - 150 °C
 12800.0 - 12800 psi

@Temperature 300 - 302 °F
 Average value: 88.3 MPa Grade Count:2
Flexural Modulus 2.94 - 3.79 GPa
426 - 550 ksi
Average value: 3.27 GPa Grade Count:5
2.55 - 2.55037 GPa

@Temperature 149 - 150 °C
 370 - 369.906 ksi

@Temperature 300 - 302 °F
 Average value: 2.55 GPa Grade Count:2
Compressive Yield Strength 76.4919 - 76.5318 MPa

@Temperature 149 - 150 °C
 11094.2 - 11100.0 psi

@Temperature 300 - 302 °F
 Average value: 76.5 MPa Grade Count:2
Shear Strength 78.5 - 78.5 MPa

@Temperature 150 - 150 °C
 11400 - 11400 psi

@Temperature 302 - 302 °F
 Average value: 78.5 MPa Grade Count:1
Izod Impact, Notched 0.883 - 1.12 J/cm
1.65 - 2.10 ft-lb/in
Average value: 0.970 J/cm Grade Count:3
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Average value: 2.00 J/cm² Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 54.0 - 55.0 µm/m-°C

@Temperature 73.0 - 200 °C
 30.0 - 30.6 µin/in-°F

@Temperature 163 - 392 °F
 Average value: 54.5 µm/m-°C Grade Count:2
CTE, linear, Transverse to Flow 55.0 - 55.0 µm/m-°C

@Temperature 200 - 200 °C
 30.6 - 30.6 µin/in-°F

@Temperature 392 - 392 °F
 Average value: 55.0 µm/m-°C Grade Count:1
Specific Heat Capacity 1.00 - 1.42256 J/g-°C

@Temperature 100 - 300 °C
 0.239 - 0.340000 BTU/lb-°F

@Temperature 212 - 572 °F
 Average value: 1.21 J/g-°C Grade Count:2
Deflection Temperature at 0.46 MPa (66 psi) 145 - 252 °C
293 - 485 °F
Average value: 200 °C Grade Count:4
Vicat Softening Point 130 - 170 °C
266 - 338 °F
Average value: 150 °C Grade Count:3
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:5
Optical Properties Metric English Comments
Refractive Index 1.51 - 1.54
1.51 - 1.54
Average value: 1.53 Grade Count:3
Transmission, Visible 90.0 %
90.0 %
Average value: 90.0 % Grade Count:3