Overview of materials for Phenolic, Novolac, Woodflour Filled

Category Polymer , Thermoset , Phenolic , Phenolic, Novolac, Woodflour Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Phenolic, Novolac, Woodflour Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Woodflour Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.36 - 1.43 g/cc
0.0491 - 0.0517 lb/in³
Average value: 1.40 g/cc Grade Count:31
Apparent Bulk Density 0.560 - 0.620 g/cc
0.0202 - 0.0224 lb/in³
Average value: 0.593 g/cc Grade Count:6
Water Absorption 0.247 - 0.640 %
0.247 - 0.640 %
Average value: 0.387 % Grade Count:31
Linear Mold Shrinkage 0.00340 - 0.0109 cm/cm
0.00340 - 0.0109 in/in
Average value: 0.00668 cm/cm Grade Count:31
Mechanical Properties Metric English Comments
Hardness, Rockwell E 75.0 - 93.0
75.0 - 93.0
Average value: 86.8 Grade Count:25
Tensile Strength, Ultimate 45.0 - 64.0 MPa
6530 - 9280 psi
Average value: 54.5 MPa Grade Count:31
Elongation at Break 0.410 - 0.920 %
0.410 - 0.920 %
Average value: 0.738 % Grade Count:25
Modulus of Elasticity 7.60 - 9.40 GPa
1100 - 1360 ksi
Average value: 8.40 GPa Grade Count:25
Flexural Yield Strength 68.0 - 97.0 MPa
9860 - 14100 psi
Average value: 83.4 MPa Grade Count:31
Flexural Modulus 6.80 - 9.00 GPa
986 - 1310 ksi
Average value: 7.82 GPa Grade Count:31
Compressive Yield Strength 155 - 234 MPa
22500 - 33900 psi
Average value: 208 MPa Grade Count:31
Poissons Ratio 0.330 - 0.360
0.330 - 0.360
Average value: 0.352 Grade Count:11
Shear Modulus 2.79 - 3.22 GPa
405 - 467 ksi
Average value: 3.00 GPa Grade Count:11
Izod Impact, Notched 0.153 - 0.241 J/cm
0.287 - 0.451 ft-lb/in
Average value: 0.187 J/cm Grade Count:25
Charpy Impact, Notched 0.178 - 0.249 J/cm²
0.847 - 1.19 ft-lb/in²
Average value: 0.196 J/cm² Grade Count:25
Thermal Properties Metric English Comments
CTE, linear 43.0 - 99.0 µm/m-°C

@Temperature 40.0 - 130 °C
23.9 - 55.0 µin/in-°F

@Temperature 104 - 266 °F
Average value: 62.3 µm/m-°C Grade Count:22
Thermal Conductivity 0.340 - 0.440 W/m-K

@Temperature 100 - 100 °C
2.36 - 3.05 BTU-in/hr-ft²-°F

@Temperature 212 - 212 °F
Average value: 0.384 W/m-K Grade Count:15
Maximum Service Temperature, Air 187 - 207 °C
369 - 405 °F
Average value: 198 °C Grade Count:25
Deflection Temperature at 1.8 MPa (264 psi) 142 - 186 °C
288 - 367 °F
Average value: 168 °C Grade Count:31
UL RTI, Electrical 150 °C
302 °F
Average value: 150 °C Grade Count:6
UL RTI, Mechanical with Impact 150 °C
302 °F
Average value: 150 °C Grade Count:6
UL RTI, Mechanical without Impact 150 °C
302 °F
Average value: 150 °C Grade Count:6
Flammability, UL94 HB - V-1
HB - V-1
Grade Count:29
Oxygen Index 24.5 - 29.1 %
24.5 - 29.1 %
Average value: 26.4 % Grade Count:23
Electrical Properties Metric English Comments
Electrical Resistivity 1.60e+11 - 5.00e+13 ohm-cm
1.60e+11 - 5.00e+13 ohm-cm
Average value: 2.81e+12 ohm-cm Grade Count:30
Dielectric Constant 4.00 - 6.10
4.00 - 6.10
Average value: 5.09 Grade Count:30
Dielectric Strength 8.50 - 16.7 kV/mm
216 - 424 kV/in
Average value: 12.0 kV/mm Grade Count:30
Dissipation Factor 0.0300 - 0.100
0.0300 - 0.100
Average value: 0.0531 Grade Count:30
Arc Resistance 25.0 - 144 sec
25.0 - 144 sec
Average value: 119 sec Grade Count:24
Comparative Tracking Index 125 - 200 V
125 - 200 V
Average value: 160 V Grade Count:30