Objet FullCure® 870 Vero Black Resin for Rapid Prototyping
| Category | Polymer , Rapid Prototyping Polymer |
| Manufacturer | Objet |
| Trade Name | FullCure® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Objet FullCure® 870 Vero Black Resin for Rapid Prototyping.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by American Precision Prototyping, LLC
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | |
| Tensile Strength, Ultimate | 50.7 MPa | 7350 psi | ASTM D638-03 |
| Elongation at Break | 17.7 % | 17.7 % | ASTM D412 |
| Tensile Modulus | 2.192 GPa | 317.9 ksi | ASTM D638-04 |
| Flexural Strength | 79.6 MPa | 11500 psi | ASTM D790-03 |
| Flexural Modulus | 2.276 GPa | 330.1 ksi | ASTM D790-04 |
| Izod Impact, Notched | 0.239 J/cm | 0.448 ft-lb/in | ASTM D256-06 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 47.0 °C | 117 °F | ASTM D648-06 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.9 °C | 109 °F | ASTM D648-06 |
| Glass Transition Temp, Tg | 62.7 °C | 145 °F | DMA, E" |
Users viewing this material also viewed the following:
- Petromont 1201 High Density Polyethylene Resin
- Chevron Phillips MA9545 HIPS - High Impact Polystyrene (discontinued **)
- Total Lacqtene® 2006 TN 35 HDPE pipe coating (discontinued **)
- Techmer ES HiFill® PA6 GF40 L 40% Milled Glass
- Wellman Wellamid® XT1816-BK1 Toughened Nylon 66
- Aclo Accutech Polypropylene Copolymer CP0437T10L Talc Reinforced
- Alliance Polymers Viprene™ G40D-22U-NAT Thermoplastic Vulcanizate Elastomer
- Ashley Polymers Ashlene® 525-13G Nylon 66, 13% Glass Reinforced
- A. Schulman ComAlloy Hiloy® 273 Polystyrene Alloy, Glass Reinforced, Flow Enhanced
- 3M 6035PC 12026 Polyurethane Foam Tape (15 lb./ft3 (239 kg/m3) Series)
Copyright © lookpolymers.com All Rights Reserved