Network Polymers Softflex® 2701T Transparent
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 2701T Transparent.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.994 g/cc | 0.994 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.17 mm |
0.0080 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 1.00 kg, Temperature 235 °C |
5.0 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 45 - 55 | 45 - 55 | 10 second dwell; ASTM D2240 |
| 48 - 58 | 48 - 58 | Instantaneous; ASTM D2240 | |
| Tensile Strength, Yield | 11.33 MPa | 1643 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 873 % | 873 % | ASTM D412 |
| 50% Modulus | 0.00150 GPa | 0.218 ksi | ASTM D412 |
| 100% Modulus | 0.00200 GPa | 0.290 ksi | ASTM D412 |
| 300% Modulus | 0.00340 GPa | 0.493 ksi | ASTM D412 |
| Gardner Impact | 27.0 J @Temperature -30.0 °C |
19.9 ft-lb @Temperature -22.0 °F |
ASTM D5420 |
| Taber Abrasion, mg/1000 Cycles | 0.0589 | 0.0589 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 22 % | 22 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
| 72.5 % @Temperature 70.0 °C |
72.5 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| 89.2 % @Temperature 100 °C |
89.2 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| Tensile Set | 3.8 % | 3.8 % |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- Polymer Resources PC-GP3-TFE5 Polycarbonate, 5% PTFE, High Flow, Wear Resistant
- DuPont Performance Polymers Crastin® S650FR BK851 PBT (Unverified Data**)
- Polimeri Europa Dutral® CO 059 Ethylene - Propylene
- Oxford Polymers PEI 1010 PEI
- Polyram Polytron A30B02 Nylon 66, 30% Long Fiber
- DSM Stanyl® TW200B6 PA46-CF30
- Dow DOWLEX™ 2035 Linear Low Density Polyethylene, Cast Film Grade
- ATI Allvac® VascoMax® C-250 Specialty Steel, Heat Treatment: 927°C (1700°F) + Age
- 3M Dyneon™ PVDF 31508/0001 Polyvinylidene Fluoride (discontinued **)
- SABIC Innovative Plastics ULTEM AR9100 PEI
Copyright © lookpolymers.com All Rights Reserved