Gouda Vuurvast AK 65 A Dense Refractory Brick
| Category | Ceramic , Oxide , Aluminum Oxide , Silicon Oxide |
| Manufacturer | Gouda Vuurvast |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gouda Vuurvast AK 65 A Dense Refractory Brick.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: This andalusite based brick with a very pure mullite bond has a low alkali and iron content. In addition, it has a high creep resistance and is therefore used in applications where load bearing capacity at high temperatures is required.Remarks: This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.60 g/cc | 0.0939 lb/in³ | Apparent |
| Porosity | 15 % | 15 % | Apparent |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Compressive Strength | 60.0 MPa | 8700 psi | Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.93 W/m-K @Temperature 650 °C |
13.4 BTU-in/hr-ft²-°F @Temperature 1200 °F |
|
| 1.93 W/m-K @Temperature 1100 °C |
13.4 BTU-in/hr-ft²-°F @Temperature 2010 °F |
||
| 1.95 W/m-K @Temperature 100 °C |
13.5 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
| Maximum Service Temperature, Air | 1700 °C | 3090 °F | |
| 1720 °C | 3130 °F | Deformation under load - t<sub>a</sub> |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 65 % | 65 % | |
| Fe2O3 | <= 1.0 % | <= 1.0 % | |
| SiO2 | 32 % | 32 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Segercone | 38 | |
| Thermal Shock Resistance | 30 cycles | DIN 51068 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 6821 C BLK
- LATI LAESTRA E01 G/30 30% Glass Fiber Reinforced, Elastomer Modified Syndiotactic Polystyrene (SPS) (disconti
- Fiberfil® J-69/10/E/UV High performance polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled, UV Stabilized
- Fiberfil® PP-60/TC/40 Polypropylene Homopolymer, 40% Talc Filled
- Industeel FORA 500 500 HB Wear Resistant Steel
- SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Asia Pacific)
- Dyna-Purge® V Purging Compound
- SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10
- Polyram RamTal RM7009 Acetal, UV Stabilized
- China Tungsten YT712 Tungsten Carbide
Copyright © lookpolymers.com All Rights Reserved