NOVA Chemicals Surpass® FPs236-A Octene sMDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® FPs236-A Octene sMDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FPs236-A complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. FPs236-A is subject to the specific limitation that it may contact food only at temperatures of 212°F and below.NOVA Chemicals' polyethylene resins are biologically and chemically inert.Features: Excellent tensile and elongation properties, Good optical properties, Low gel levelAdditives: High temperature AOApplications: Cast film, Co-extrusion and laminationFilm properties are typical of cast film extruded at a melt temperature of 500°F, and a line speed of 600 ft/min.
Physical Properties Metric English Comments
Density 0.936 g/cc
0.0338 lb/in³
ASTM D 792
Thickness 25.0 microns
0.984 mil
As tested for properties on this data sheet
Melt Flow 2.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 14.2 MPa
2060 psi
ASTM D 882
Film Tensile Strength at Yield, TD 15.1 MPa
2190 psi
ASTM D 882
Film Elongation at Break, MD 600 %
600 %
ASTM D 882
Film Elongation at Break, TD 900 %
900 %
ASTM D 882
Elmendorf Tear Strength MD 40 g
40 g
ASTM D 1922
Elmendorf Tear Strength TD 350 g
350 g
ASTM D 1922
Elmendorf Tear Strength, MD 1.60 g/micron
40.6 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 14.0 g/micron
356 g/mil
ASTM D 1922
Dart Drop 1.60 g/micron
40.6 g/mil
ASTM D 1709/A
Dart Drop Test 40.0 g
0.0882 lb
F50; ASTM D 1709/A
Film Tensile Strength at Break, MD 45.0 MPa
6530 psi
ASTM D 882
Film Tensile Strength at Break, TD 35.0 MPa
5080 psi
ASTM D 882
1% Secant Modulus, MD 300 MPa
43500 psi
ASTM D 882
1% Secant Modulus, TD 370 MPa
53700 psi
ASTM D 882
Optical Properties Metric English Comments
Haze 4.8 %
4.8 %
ASTM D 1003
Gloss 80 %
80 %
At 45°; ASTM D 2457
Descriptive Properties Value Comments
Low Friction Puncture 24 (J/mm)
NOVA Chemicals test method