NOVA Chemicals Sclair® TD-7915-UG Hexene MDPE Rotational Molding Resin  (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	NOVA Chemicals Sclair® TD-7915-UG Hexene MDPE Rotational Molding Resin  (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Excellent low temperature impact properties, Excellent ESCR, Wide process window, NSF listing for Stds. 14, 24, and 61 pending, Retention of impact at long cook timesApplications: IBCs, Toys, General purpose custom molding, Agricultural storage tanks, Marine partsAdditives: Processing antioxidants, UV stabilizersInformation provided by NOVA Chemicals.

Physical Properties	Metric	English	Comments
Density	0.935 g/cc	0.0338 lb/in³	ASTM D792
ESCR 100% Igepal®	>= 1000 hour <br>@Temperature 50.0 °C	>= 1000 hour <br>@Temperature 122 °F	F<sub>50</sub>; Condition A, From compression molded specimens; ASTM D1693
ESCR 10% Igepal®	140 hour <br>@Temperature 50.0 °C	140 hour <br>@Temperature 122 °F	F<sub>50</sub>; Condition A, From compression molded specimens; ASTM D1693
Melt Flow	5.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C	5.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	17.3 MPa <br>@Thickness 3.17 mm	2510 psi <br>@Thickness 0.125 in	Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638
Flexural Modulus	0.780 GPa	113 ksi	1% Strain Value from rotomolded samples; ASTM D790
Impact Test	67.8 J <br>@Thickness 3.17 mm,<br> Temperature -40.0 °C	50.0 ft-lb <br>@Thickness 0.125 in,<br> Temperature -40.0 °F	rotomolded; ARM Method
	217 J <br>@Thickness 6.35 mm,<br> Temperature -40.0 °C	160 ft-lb <br>@Thickness 0.250 in,<br> Temperature -40.0 °F	rotomolded; ARM Method

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	47.0 °C	117 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	37.3 °C	99.1 °F	ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	204 - 315 °C	399 - 599 °F	Varies with the mold shape and construction. Oven will also affect process time.

Users viewing this material also viewed the following:

NOVA Chemicals Sclair® TD-7915-UG Hexene MDPE Rotational Molding Resin &nbsp;(discontinued **)

NOVA Chemicals Sclair® TD-7915-UG Hexene MDPE Rotational Molding Resin (discontinued **)