- NOVA Chemicals Sclair® 59D HDPE Blow Molding Resin (discontinued **)
NOVA Chemicals Sclair® 59D HDPE Blow Molding Resin (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 59D HDPE Blow Molding Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: High impact resistance, good stiffness, moderate ESCR.Applications: Food packaging, small parts (HIC), oil bottles.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | 75 hour | 75 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 0.28 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.28 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Yield | 31.5 MPa | 4570 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 205 °C | 320 - 401 °F |
Users viewing this material also viewed the following:
- Nylacast Nylube MO Cast Nylon 6, Lubricated (Blended Solid and Liquid Lubricant), MoS2 Filled
- SABIC Innovative Plastics LNP COLORCOMP R1000 PA 66
- ExxonMobil LL 1235x70 Cast Film Resin (discontinued **)
- Arkema Group Oroglas® MI-2T Acrylic (discontinued **)
- M. Holland Company CP300 Polypropylene Copolymer
- Huntsman Matrimid 5218 Resin
- Techmer ES HiFill® PA6 GF50 IM2 L 50% Glass Filled (Dry)
- A. Schulman POLYBLAK™ 4479-01 Black Color Concentrate, 50% Carbon Black Based In LLDPE
- DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved