NIZHNEKAMSKNEFTEKHIM PE 5117N (18601) Linear Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 5117N (18601) Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 - 0.920 g/cc | 0.0331 - 0.0332 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| 24 - 36 g/10 min @Load 21.6 kg, Temperature 190 °C |
24 - 36 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 50.0 MPa | >= 7250 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 35.0 MPa | >= 5080 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 700 % | >= 700 % | ASTM D882 |
| Film Elongation at Break, TD | >= 950 % | >= 950 % | ASTM D882 |
| Tensile Modulus | >= 0.130 GPa | >= 18.9 ksi | 2% sec, MD; ASTM D882 |
| >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 9.45 g/micron | >= 240 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 18.9 g/micron | >= 480 g/mil | ASTM D1922 |
| Dart Drop Test | >= 210 g | >= 0.463 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 0 | > 1mm |
| 245 | (0.2-0.5)mm | |
| 250 | > 0.2mm (totally) | |
| 5 | (0.5-1.0)mm |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 18 FRT 5 PP, mod. of mech. properties, fire retardant
- Quadrant EPP Ketron® CM GF30 Compression Molded, 30% Glass Reinforces Polyethererther Ketone(ASTM Product Data Sheet)
- Shakespeare MX-200 PP Polypropylene Monofilament
- A. Schulman POLYBATCH™ Weathered Wood 10418U Concentrate Based In LLDPE
- Eastman Tenite Propionate 377E4861312 Clear, Trsp Cellulose Acetate Propionate
- Equate EMDA-6147 HDPE Blow Molding Resin
- Arkema Group ORGASOL® 2002 ES 4 Nat 3 Polyamide 12
- Arlon 28540R015 0.016" (0.406 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M 5425 UHMW Polyethylene Tape
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-550 (FEF)
Copyright © lookpolymers.com All Rights Reserved