NIZHNEKAMSKNEFTEKHIM PE 4115P (16402) Linear Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 4115P (16402) Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.914 - 0.918 g/cc | 0.0330 - 0.0332 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| 54 - 66 g/10 min @Load 21.6 kg, Temperature 190 °C |
54 - 66 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 44.0 MPa | >= 6380 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 30.0 MPa | >= 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 550 % | >= 550 % | ASTM D882 |
| Film Elongation at Break, TD | >= 820 % | >= 820 % | ASTM D882 |
| Tensile Modulus | >= 0.120 GPa | >= 17.4 ksi | 2% sec, MD; ASTM D882 |
| >= 0.130 GPa | >= 18.9 ksi | 2% sec, TD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 4.72 g/micron | >= 120 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 15.0 g/micron | >= 380 g/mil | ASTM D1922 |
| Dart Drop Test | >= 95.0 g | >= 0.209 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 0 | > 1mm |
| 245 | (0.2-0.5)mm | |
| 250 | > 0.2mm (totally) | |
| 5 | (0.5-1.0)mm |
Users viewing this material also viewed the following:
- Garlock 5260 Neoprene Sheet Rubber
- Sharadaa Ceramics ZAP 009 Smart Cast Application
- Zhejiang Juner PC-A6-2 Top-Grade Flame Retardant UV-Resistant
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Fiber Reinforced, Heat Impact Nylon 6
- DayGlo Phantom IPO-15 Invisible Pigment, Orange
- DuPont Teijin Films Melinex® 339 Polyester Film, 700 Gauge
- Chosun Refractories PTC-165 Plastic Refractory
- BASF Ultramid® 8202 L Intermediate PA6 (Dry)
- AorTech Biomaterials ECSil™ 60D Biomedical Carbonate Silicone Pellets
- ChevronTexaco ISO 220 Ultra Gear Lubricant
Copyright © lookpolymers.com All Rights Reserved