- Multibase Multi-Flex® TPO D-5016
Multibase Multi-Flex® TPO D-5016
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPO |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPO D-5016.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Multi-Flex® D-5016 is an elastomer modified polypropylene for applications requiring elastomeric properties and good molding behavior.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D792-91 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955-89 |
| Melt Flow | 16 g/10 min | 16 g/10 min | (Condition L) ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | 10 sec; ASTM D-2240-95 |
| Tensile Strength, Ultimate | 16.6 MPa | 2410 psi | 20" / min.; ASTM D-683-95 |
| Elongation at Break | 1300 % | 1300 % | ASTM D638-95 |
| Izod Impact, Notched | NB | NB | ASTM D-256-93a |
| Tear Strength | 116 kN/m | 662 pli | ASTM D624-95 |
Users viewing this material also viewed the following:
- MV Labs HG100 Hg(C2H3O2)2 Mercury(II) acetate
- Premix Premi-Glas® 2204-22 CR-SX Fiberglass Reinforced SMC
- Momentive Performance Materials RTV88 Silicone Rubber Compound for High Temperature, Red
- Garlock 681 Vegetable Fiber Gasketing
- Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F)
- Universal Wire Works 410 Stainless Steel (AMS 5776) Filler Metal
- ChevronTexaco ISO 100 Utility Oil LVI
- ExxonMobil 60 Mobilube XFD
- LATI LARIL 13 G/30 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (Unverified Data**)
- LNP Verton™ UF-700-10 Polyphthalamide, Long Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved