Multibase Multi-Flex® D 5500 TPO Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyolefin |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® D 5500 TPO Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms: PelletsProcessing Methods:Blow MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM 792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | 10 seconds; ASTM D2240 |
| Tensile Strength, Yield | 21.7 MPa | 3150 psi | Elastic; ASTM D638 |
| Elongation at Break | 850 % | 850 % | ASTM D638 |
| Flexural Modulus | 0.607 GPa | 88.0 ksi | ASTM D790 |
| Tear Strength | 158 kN/m | 900 pli | ASTM D624 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 80A, Non-Black Sulfur Cure
- SABIC Innovative Plastics LNP LUBRICOMP CBL36XXC PS
- Forever Plast Namtene® 1002 Recycled Pipe Grade HDPE
- Dow Corning C6-550 LIQUID SILICONE RUBBER KIT
- ChevronTexaco Rykon® ISO 68 Oil AW
- Arlon LW201B##-P2 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported)
- Momentive Performance Materials Silopren™ LSR 4060 Liquid Silicone Rubber - Healthcare
- PolyOne Edgetek® MLS-XC195C-2 Polysulfone Alloy - ESD Material - Lubricated (discontinued **)
- SABIC Innovative Plastics LNP Thermocomp TX88477 PU
- LyondellBasell Hifax™ ETA-3163UV Thermoplastic Olefin Resin
Copyright © lookpolymers.com All Rights Reserved