Multibase C6-180 Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-180 Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 77
77
no post cure; ASTM D2240
82
82
post cured- 2 hours at 177°C; ASTM D2240
83
83
post cured- 4 hours at 177°C; ASTM D2240
85
85
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 6.61 MPa
958 psi
post cured- 8 hours at 177°C; ASTM D412
7.226 MPa
1048 psi
post cured- 4 hours at 177°C; ASTM D412
7.233 MPa
1049 psi
no post cure; ASTM D412
7.350 MPa
1066 psi
post cured- 2 hours at 177°C; ASTM D412
Tensile Strength, Yield 3.68 MPa
534 psi
at 200%, no post cure; ASTM D412
4.05 MPa
587 psi
200%, post cured- 4 hours at 177°C; ASTM D412
4.07 MPa
590 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
4.40 MPa
638 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 387 %
387 %
post cured- 8 hours at 177°C; ASTM D412
481 %
481 %
post cured- 4 hours at 177°C; ASTM D412
500 %
500 %
post cured- 2 hours at 177°C; ASTM D412
614 %
614 %
no post cure; ASTM D412
Tear Strength 21.2 kN/m
121 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
22.3 kN/m
127 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
22.4 kN/m
128 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
39.1 kN/m
223 pli
Die B, no post cure; ASTM D624
Thermal Properties Metric English Comments
Shrinkage 1.8 %
1.8 %
no post cure
2.60 %

@Temperature 177 °C,
Time 7200 sec
 2.60 %

@Temperature 351 °F,
Time 2.00 hour
 post cured
2.60 %

@Temperature 177 °C,
Time 14400 sec
 2.60 %

@Temperature 351 °F,
Time 4.00 hour
 post cured
2.80 %

@Temperature 177 °C,
Time 28800 sec
 2.80 %

@Temperature 351 °F,
Time 8.00 hour
 post cured