Multibase C6-150 Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-150 Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 50
50
no post cure; ASTM D2240
59
59
post cured- 2 hours at 177°C; ASTM D2240
60
60
post cured- 4 hours at 177°C; ASTM D2240
61
61
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 9.115 MPa
1322 psi
post cured- 4 hours at 177°C; ASTM D412
9.453 MPa
1371 psi
post cured- 2 hours at 177°C; ASTM D412
9.694 MPa
1406 psi
post cured- 8 hours at 177°C; ASTM D412
10.65 MPa
1545 psi
no post cure; ASTM D412
Tensile Strength, Yield 1.94 MPa
282 psi
at 200%, no post cure; ASTM D412
2.69 MPa
390 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
2.83 MPa
410 psi
200%, post cured- 4 hours at 177°C; ASTM D412
2.95 MPa
428 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 659 %
659 %
post cured- 8 hours at 177°C; ASTM D412
675 %
675 %
post cured- 4 hours at 177°C; ASTM D412
730 %
730 %
post cured- 2 hours at 177°C; ASTM D412
976 %
976 %
no post cure; ASTM D412
Tear Strength 41.0 kN/m
234 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
42.8 kN/m
244 pli
Die B, no post cure; ASTM D624
43.6 kN/m
249 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
45.8 kN/m
261 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
Thermal Properties Metric English Comments
Shrinkage 2.4 %
2.4 %
no post cure
2.80 %

@Temperature 177 °C,
Time 7200 sec
 2.80 %

@Temperature 351 °F,
Time 2.00 hour
 post cured
3.00 %

@Temperature 177 °C,
Time 14400 sec
 3.00 %

@Temperature 351 °F,
Time 4.00 hour
 post cured
3.10 %

@Temperature 177 °C,
Time 28800 sec
 3.10 %

@Temperature 351 °F,
Time 8.00 hour
 post cured