Mitsubishi Hostaphan® WN, 190 micron Nominal Thickness Translucent White Polyethylene Terephthalate Film

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer Mitsubishi
Trade Name Hostaphan®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Mitsubishi Hostaphan® WN, 190 micron Nominal Thickness Translucent White Polyethylene Terephthalate Film.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Hostaphan® WN is a white film made of polyethylene terephthalate (PET) and is well suited for electrical insulating of machines and appliances. The high dielectric strength and large volume resistance of Hostaphan® WN make it possible to use the film as a high-quality insulation material. Applications:Insulation of winding headsSingle phase insulationSlot insulationBallastsInformation provided by Mitsubishi Polyester Film
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.010 cm/cm
<br>@Temperature 150 °C,<br> Time 900 sec
 0.010 in/in
<br>@Temperature 302 °F,<br> Time 0.250 hour
 DIN 40634
Linear Mold Shrinkage, Transverse 0.010 cm/cm
<br>@Temperature 150 °C,<br> Time 900 sec
 0.010 in/in
<br>@Temperature 302 °F,<br> Time 0.250 hour
 DIN 40634
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
<br>@Temperature 150 °C
 1.00e+12 ohm-cm
<br>@Temperature 302 °F
 DC; DIN 40634 or VDE 0345 in air or ASTM D257
1.00e+18 ohm-cm
<br>@Temperature 23.0 °C
 1.00e+18 ohm-cm
<br>@Temperature 73.4 °F
 DC; DIN 40634 or VDE 0345 in air or ASTM D257
Surface Resistance >= 1.00e+12 ohm
<br>@Temperature 150 °C
 >= 1.00e+12 ohm
<br>@Temperature 302 °F
 75% r.h.; DIN 53482 or VDE 0303/part 3 or ASTM D257
1.00e+14 ohm
<br>@Temperature 23.0 °C
 1.00e+14 ohm
<br>@Temperature 73.4 °F
 50% r.h.; DIN 53482 or VDE 0303/part 3 or ASTM D257
>= 5.00e+14 ohm
<br>@Temperature 23.0 °C
 >= 5.00e+14 ohm
<br>@Temperature 73.4 °F
 25% r.h.; DIN 53482 or VDE 0303/part 3 or ASTM D257
Dielectric Constant 3.3
<br>@Frequency 50.0 Hz,<br> Temperature 23.0 °C
 3.3
<br>@Frequency 50.0 Hz,<br> Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air or ASTM D150
3.3
<br>@Frequency 1000 Hz,<br> Temperature 23.0 °C
 3.3
<br>@Frequency 1000 Hz,<br> Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air or ASTM D150
3.6
<br>@Frequency 50.0 Hz,<br> Temperature 150 °C
 3.6
<br>@Frequency 50.0 Hz,<br> Temperature 302 °F
 DIN 40634 or VDE 0345 in air or ASTM D150
Dielectric Strength 420 kV/mm
<br>@Temperature 23.0 °C
 10700 kV/in
<br>@Temperature 73.4 °F
 DC; DIN 40634 or VDE 0345 in air or ASTM D149
135 kV/mm
<br>@Frequency 50.0 Hz,<br> Temperature 150 °C
 3430 kV/in
<br>@Frequency 50.0 Hz,<br> Temperature 302 °F
 DIN 40634 or VDE 0345 in air or ASTM D149
150 kV/mm
<br>@Frequency 50.0 Hz,<br> Temperature 23.0 °C
 3810 kV/in
<br>@Frequency 50.0 Hz,<br> Temperature 73.4 °F
 DIN 40634 or VDE 0345 in air or ASTM D149
Dissipation Factor 0.0020
<br>@Frequency 50.0 Hz,<br> Temperature 23.0 °C
 0.0020
<br>@Frequency 50.0 Hz,<br> Temperature 73.4 °F
 tand; DIN 40634 or VDE 0345 in air or ASTM D149
0.0048
<br>@Frequency 50.0 Hz,<br> Temperature 150 °C
 0.0048
<br>@Frequency 50.0 Hz,<br> Temperature 302 °F
 tand; DIN 40634 or VDE 0345 in air or ASTM D149
0.0052
<br>@Frequency 1000 Hz,<br> Temperature 23.0 °C
 0.0052
<br>@Frequency 1000 Hz,<br> Temperature 73.4 °F
 tand; DIN 40634 or VDE 0345 in air or ASTM D149
Descriptive Properties Value Comments
Behavior Under the Influence of Partial Discharges (Min.) 900
DIN 53485 or VDE 0303/part 7; Contact method, 40KV/mm
Conductivity of Aqueous Extract (µS/cm) 2
DIN 40634 or VDE 0345; 1 kHz
Frigen Extract (%) 0.05
DIN 8944; Cold extraction
Insulation Class in Electrical Engineering B
DIN 57530 or VDE 0530, main list
Trichloroethylene- Extract (%) 0.2
DIN 8943; Extracted in Soxhalet apparatus for 2h. Boiled down for 15h at 105ºC