Menzolit Menzolit® SMC 0400 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® SMC 0400 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SMC 0400 is a Class-A SMC for exterior body applications on cars, LCV´s and trucks. These compounds mould to parts with good up to excellent surface quality for medium bake in-line and off-line painted (100 – 140°C) body panels. Surface defects like waviness, fibre patterns and orange peel do not occur with this products. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished. To ease demoulding we highly recommend chrome-plating of tool surfaces. Menzolit® SMC 0400 allows. The product shows very good adhesion to paint or In Mould Coating (IMC). Because of its zero shrink properties warpage is eliminated and parts reproducing the dimensions of the cold mould can be produced.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | -0.000500 cm/cm | -0.000500 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 90.0 MPa @Temperature 22.0 °C |
13100 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 90.0 MPa @Temperature 22.0 °C |
13100 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 1.5 % | 1.5 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 180 MPa @Temperature 22.0 °C |
26100 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Compressive Yield Strength | 100 MPa | 14500 psi | ISO 14126 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 4.20 GPa | 609 ksi | in plane |
| Charpy Impact, Notched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 200 °C | 392 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 140 - 160 °C | 284 - 320 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- MV Labs MN820 MnO2 Manganese(IV) oxide
- Ovation Polymers Nemcon™ H ABS DP116P ABS
- Techmer ES HiFill® PA11 GB7 HS L 7% Glass Bead Filled
- Styron CALIBREâ„¢ 2060 15 Polycarbonate, Sterilization Grade
- Sumitomo Bakelite North America FM 21386 Synthetic Fiber Reinforced Phenolic Novolac
- DuPont Performance Polymers Hytrel® HTR8136BK TPC-ET (Unverified Data**)
- 3M Controltac™ RG180C-10 Graphic Film
- ExxonMobil Santoprene® 181-64MED Thermoplastic Elastomer (discontinued **)
- Fainplast Compounds RI 548/H Rigid PVC, Antishock Injection Molding
Copyright © lookpolymers.com All Rights Reserved