Manifattura Cattaneo RULON® 641 Polytetrafluoroethylene
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo RULON® 641 Polytetrafluoroethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.10 g/cc | 0.0759 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.00 % @Temperature 23.0 °C |
0.00 % @Temperature 73.4 °F |
50% RH; ASTM D570 |
| Water Absorption at Saturation | 0.00 % | 0.00 % | ASTM D570 |
| Deformation | 4.0 % @Time 86400 sec, Pressure 100 MPa |
4.0 % @Time 24.0 hour, Pressure 14500 psi |
ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D 2240 |
| Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
| Elongation at Break | 175 % | 175 % | ASTM D638 |
| Compressive Yield Strength | 4.80 MPa @Strain 1.00 %, Time 3.60e+6 sec |
696 psi @Strain 1.00 %, Time 1000 hour |
ASTM D695 |
| Compressive Modulus | 0.400 GPa | 58.0 ksi | ASTM D695 |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.10 | 0.10 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 0.13 | 0.13 | µm/s. PV = 0.1 MPa-m/s; max P = 6.9 MPa; MPC Test |
| Limiting Pressure Velocity | 0.350 MPa-m/sec | 9990 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 102 µm/m-°C @Temperature 23.0 - 100 °C |
56.7 µin/in-°F @Temperature 73.4 - 212 °F |
|
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature 23.0 °C |
41.7 µin/in-°F @Temperature 73.4 °F |
|
| Thermal Conductivity | 0.370 W/m-K | 2.57 BTU-in/hr-ft²-°F | ASTM D177 |
| Maximum Service Temperature, Air | 288 °C | 550 °F | |
| Minimum Service Temperature, Air | -240 °C | -400 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White | |
| UV Resistance | Y |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PQ 83 T 15 PP, 15% mineral filling, UV stabilization
- SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS (Asia Pacific)
- Heatbath/Park No-Carb Stop-Off/Protective Coating for Steel
- LG Chemical Lupox® GP2156FT PBT+GF15%
- SABIC Innovative Plastics LNP THERMOCOMP D7001IXH PC
- Polyram RamTal PM3007G2 Polyacetal for Injection Molding, 10% Glass Fiber Reinforced
- Ensinger Tecapeek® XP-101 Compression Molded PEEK Compound, Filled with 15% Graphite and 10% PTFE
- Diamond Polymers NPP30-2400 GF20 20% Glass Filled Homopolymer Polypropylene
- Axiall ProTherm® 4351 Rigid PVC, Extrusion
- Ascend Performance Materials Vydyne® 66J Nylon 66, General Purpose, high viscosity, Conditioned
Copyright © lookpolymers.com All Rights Reserved