- Chosun Refractories HSC-16H-W2 Dense and High-Strength Castable, Credens
Chosun Refractories HSC-16H-W2 Dense and High-Strength Castable, Credens
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-16H-W2 Dense and High-Strength Castable, Credens.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.017658 GPa @Temperature 110 °C, Time 86400 sec |
2.5611 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.01962 GPa @Temperature 1000 °C, Time 10800 sec |
2.846 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| Compressive Strength | 88.3 MPa @Temperature 110 °C, Time 86400 sec |
12800 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 93.2 MPa @Temperature 1000 °C, Time 10800 sec |
13500 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.150 % @Temperature 1350 °C, Time 10800 sec |
-0.150 % @Temperature 2460 °F, Time 3.00 hour |
|
| 0.00 % @Temperature 110 °C, Time 86400 sec |
0.00 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 57 % | 57 % | |
| CaO | 1.8 % | 1.8 % | |
| SiO2 | 38 % | 38 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating,Casting | |
| Material Required for Estimating(kg/?) | 2,560 | |
| Water Required for Casting(%) | 5.3-5.7 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GM-3968 PVC Compound
- SABIC Innovative Plastics Lexan® HFD1433 PC Copolymer (Asia Pacific)
- Indium Corp. Indalloy® 131 97Sn/3Sb Lead-Free Solder Alloy
- Techmer ES Plastiblend® ABS LG UV
- SK Chemicals SKYTHANE® 198A S series Polyurethane
- SABIC Innovative Plastics Ultem HU2410 PEI (Europe-Africa-Middle East)
- Plastics Group Polifil® RMT-40 40% Talc-Reinforced Polypropylene, High Impact
- Fainplast Compounds GS 7006 Flexible PVC, Injection Molding for Footwear
- E-Polymers SEPAZ® LH30 PP Homopolymer LFT Resin
Copyright © lookpolymers.com All Rights Reserved