Lubrizol Advanced Materials Pearlthane® ECO D12T90E Thermoplastic Polyurethane
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials Pearlthane® ECO D12T90E Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® ECO D12T90E is a 91 Shore A, High Performance natural TPU based on Renewable Sources with ca. 37% renewable content according to ASTM D6866 for Extrusion and Blow moulding applications. This natural TPU resin features properties similar to standard TPU of same hardness (i.e. excellent mechanical properties and abrasion resistance)Applications: PEARLTHANE® ECO D12T90E enhances the performance of a wide range of end use products that ranges from automotive, consumer electronics and sport and leisure applications among others where environmentally-friendly materials can bring value to the end product.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ISO 2781 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | MQSA 44 |
| Melt Flow | 10 g/10 min @Load 21.6 kg, Temperature 190 - 200 °C |
10 g/10 min @Load 47.6 lb, Temperature 374 - 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 91 | 91 | ISO 868 |
| Tensile Strength | 37.99 MPa | 5510 psi | ISO 527 |
| Tensile Strength, Yield | 9.03 MPa @Strain 100 % |
1310 psi @Strain 100 % |
ISO 527 |
| 27.03 MPa @Strain 300 % |
3920 psi @Strain 300 % |
ISO 527 | |
| Elongation at Break | 420 % | 420 % | ISO 527 |
| Tear Strength | 119 kN/m | 679 pli | Die C; ISO 34-1B |
| Abrasion | 3.0 | 3.0 | mm<sup>3</sup> Loss; ISO 4649 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 190 - 200 °C | 374 - 392 °F | Temperature range at which MFI = 10 g/10 min at 21.6 kg.; MQSA 111 |
| Glass Transition Temp, Tg | -40.6 °C | -41.0 °F | DSC, 50°F/min; DIN 51.007 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 200 - 210 °C | 392 - 410 °F | |
| Zone 2 | 210 - 220 °C | 410 - 428 °F | |
| Zone 3 | 220 - 230 °C | 428 - 446 °F | |
| Zone 4 | 210 - 220 °C | 410 - 428 °F | |
| Die Temperature | 200 - 210 °C | 392 - 410 °F | |
| Screw Speed | 50 rpm | 50 rpm |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 15A Butene HDPE Film Resin
- Iran Petrochemical (PCC) TPC - 323 FC Expandable Polystyrene
- Techmer ES Electrafil® J-50/CF/20/TF/15 Polycarbonate, 20% Carbon Fiber Reinforced, 15% PTFE
- Solvay Specialty Polymers Veradel® 3200P Polyethersulfone (PESU)
- A. Schulman POLYBATCH™ Brown 1028 Concentrate Based In Polyethylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR DBPH-50
- Alliance Polymers Viprene™ G55A-32U-BLK Thermoplastic Vulcanizate Elastomer
- 3M 551 Polyurethane Adhesive Sealant
- Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength (Unverified Data**)
- Loctite® 574 Semi-rigid Cure Anaerobic Sealant
Copyright © lookpolymers.com All Rights Reserved