Lubrizol Advanced Materials PEARLTHANE® D11H95S Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials PEARLTHANE® D11H95S Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® D11H95S is a high performance polycaprolactone copolyester based TPU, supplied in form of translucent, colorless pellets, featuring excellent flow and mechanical properties and an outstanding low compression set value and high temperature resistance. Product recommended for injection-molding applications with an extremely short cycle time.All information provided by Merquinsa
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg, Temperature 215 - 225 °C |
10 g/10 min @Load 46.6 lb, Temperature 419 - 437 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 47 | 47 | ASTM D2240 |
| Tensile Strength, Yield | 50.00 MPa | 7252 psi | ASTM D412 |
| Elongation at Break | 505 % | 505 % | ASTM D412 |
| 100% Modulus | 0.01100 GPa | 1.595 ksi | ASTM D412 |
| 300% Modulus | 0.02200 GPa | 3.191 ksi | ASTM D412 |
| Tear Strength | 166 kN/m | 948 pli | ASTM D624 (Die C) |
| Abrasion | 25 | 25 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 15 % @Temperature 23.0 °C, Time 252000 sec |
15 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395B |
| 21 % @Temperature 70.0 °C, Time 79200 sec |
21 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395B | |
| 32 % @Temperature 100 °C, Time 252000 sec |
32 % @Temperature 212 °F, Time 70.0 hour |
ASTM D395B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 - 225 °C | 419 - 437 °F | MQSA 111 |
| Glass Transition Temp, Tg | -36.1 °C | -33.0 °F | DSC, 50ºF / min.; ISO11357-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 200 °C | 392 °F | |
| Nozzle Temperature | 210 °C | 410 °F | |
| Zone 1 | 205 °C | 401 °F | Compression Zone |
| Zone 2 | 205 °C | 401 °F | Metering Zone |
| Mold Temperature | 35.0 °C | 95.0 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | MQSA 44 |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 12, 50% Glass Fiber Filled
- Kazanorgsintez Polyethyleneglycol-9
- Solvay TECHNYL® C 507XT PA6, Conditioned
- SABIC Innovative Plastics Noryl GTX GTX8110P PPE+PA (Europe-Africa-Middle East)
- SK Chemicals SKYTHANE® R195A Polyether Based Thermoplastic Polyurethane Elastomer
- Teknor Apex APEX® 80459 Polyvinyl Chloride, Flexible
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 66A
- Dow Corning SE 4430 KIT
- DuPont Performance Polymers Zytel® 103HSL NC010 Nylon 66 (Unverified Data**)
- 3M Scotchcal™ ElectroCut™ 7725-196 Graphic Film
Copyright © lookpolymers.com All Rights Reserved