- Lubrizol Advanced Materials PEARLTHANE® 12F75UV Thermoplastic Polyurethane Elastomer
Lubrizol Advanced Materials PEARLTHANE® 12F75UV Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials PEARLTHANE® 12F75UV Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® D12F75UV is a UV resistant standard polyester based TPU supplied in form of translucent, colorless or slightly yellowish pellets, featuring a low melting point and very low gel content. Processed by extrusion and compounding. PEARLTHANE® D12F75UV is designed for a wide variety of adhesive film applications requiring excellent adhesion in combination with good heat resistance. This grade can be both cast extruded and blown.All information provided by Merquinsa
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg |
10 g/10 min @Load 47.6 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | ASTM D2240 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D412 |
| Elongation at Break | 620 % | 620 % | ASTM D412 |
| 100% Modulus | 0.00500 GPa | 0.725 ksi | ASTM D412 |
| 300% Modulus | 0.00650 GPa | 0.943 ksi | ASTM D412 |
| Tear Strength | 155 kN/m | 885 pli | ASTM D624 (Die C) |
| Abrasion | 35 | 35 | loss (mm³); DIN 53.516 |
| Compression Set | 30 % @Temperature 22.8 °C, Time 252000 sec |
30 % @Temperature 73.0 °F, Time 70.0 hour |
ASTM D395 |
| 55 % @Temperature 70.0 °C, Time 86400 sec |
55 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 130 - 140 °C | 266 - 284 °F | MQSA 111 |
| Glass Transition Temp, Tg | -30.0 °C | -22.0 °F | DSC, 10ºC/min; DIN 51.007 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 145 - 155 °C | 293 - 311 °F | |
| Zone 2 | 155 - 165 °C | 311 - 329 °F | |
| Zone 3 | 165 - 175 °C | 329 - 347 °F | |
| Zone 4 | 170 - 180 °C | 338 - 356 °F | |
| Die Temperature | 170 - 180 °C | 338 - 356 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | MQSA 44 |
Users viewing this material also viewed the following:
- Sylvin Technologies 8980-95 Natural PVC Extrusion Compound
- Solvay TECHNYL® A 60 G1 V30 PA66, 30% glass fiber, Conditioned
- Solvay Chemicals Grade A Barium Hydroxide Octahydrate
- Samsung Cheil Industries Infino® HI-1001BG PC/ABS, Metal Plating Grade
- Fainplast Compounds FR 85 Flexible PVC, Insulation
- ChevronTexaco Rykon® 1426 Premium Grease
- Ametek High Purity Nickel Strip 899M Hard
- Chevron Phillips 6109M LLDPE Blown Film Resin, Butene Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved