Loxim 830 01 HB Polypropylene Compound, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 830 01 HB Polypropylene Compound, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 - 1.15 g/cc | 1.05 - 1.15 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 - 55.0 MPa | 7250 - 7980 psi | ASTM D683 |
| Elongation at Break | 8.0 - 10 % | 8.0 - 10 % | ASTM D638 |
| Flexural Modulus | 4.00 - 4.50 GPa | 580 - 653 ksi | ASTM D790 |
| Izod Impact, Notched | 0.550 - 0.650 J/cm | 1.03 - 1.22 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 - 135 °C | 257 - 275 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Ineos Nova T163B Expandable Polystyrene
- Momentive Performance Materials RTV60 Silicone Rubber Compound for High Temperature, Red
- SABIC Innovative Plastics Ultem 2200N PEI (Asia Pacific)
- Solvay Specialty Polymers Halar® 9414 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE), Filled
- Tipco Tipcolite® TPF 550 - Unreinforced Phenolic Resin having 41 mm Norton Flow with 9% Hexamine
- ExxonMobil 30 Mobiltrans HD
- Arlon 0.008" (0.2032 mm) Thermabond® Uncured Silicone (99510N008)
- BASF Ultramid® A3UG5 BK 23260 25% Glass Filled PA66 (Conditioned)
- DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved