Lord Adhesives 8611 Polymer Resistor Composition
| Category | Polymer , Thermoset |
| Manufacturer | Lord Adhesives |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives 8611 Polymer Resistor Composition.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LORD 8600 series polymer resistor compositions are designed for screen print application onto a wide range of substrates.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Brookfield Viscosity | 20000 - 40000 cP @Temperature 25.0 °C |
20000 - 40000 cP @Temperature 77.0 °F |
HBT, Spindle CP-51 @ 1rpm |
| Thickness | 14.0 - 18.0 microns | 0.551 - 0.709 mil |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 9.0 - 11 ohm | 9.0 - 11 ohm | Cured on alumina substrate @ 210ºC for 30 min; Termination: LORD 3504 Palladium Silver Conductor; Resistor Geometry: 1mm x 1mm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 30.0 min @Temperature 210 °C |
0.500 hour @Temperature 410 °F |
|
| Shelf Life | 6.00 Month @Temperature 25.0 °C |
6.00 Month @Temperature 77.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black | |
| Consistency | Paste | |
| Thermal Coefficient of Resistance (ppm/ºC) | <650 | Cold TCR measured @ -55 to 25ºC; Hot TCR measured @ 25º to 125ºC |
| Typical Resistance Change (%) | <10 | Moisture Resistance: Resistance change on 1mm x 1mm resistor after 1 hour in a pressure cooker |
| <2 | Electrostatic Discharge: Resistance change after two 2000 volt pulses on 1mm x 1mm resistor |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL® 6330 Conductive Elastomer
- Overview of materials for Nylon 66, 30% Glass Fiber Filled
- Lord Adhesives 648 Low Odor, Low Flammability, Non Sag, Metal Use Acrylic Adhesive
- Teknor Apex APEX® 82-E254NL-9 Polyvinyl Chloride, Flexible
- Master Bond Supreme 3HT-80 One Component, Toughened, Heat Curing Epoxy
- DuPont™ Kapton® 500A Polyimide Film, 125 Micron Thickness
- Entec Hyrene® PSCRY 2.5 General Purpose Polystyrene
- Fainplast Compounds POLIFAIN 6020 Flexible PVC, Injection Molding for Footwear
- ExxonMobil Santoprene® 101-87 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved