LNP Lubricomp® OCL-4036 Polyphenylene Sulfide, Carbon Fiber Reinforcement, PTFE Lubricant  (discontinued **)&l

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® OCL-4036 Polyphenylene Sulfide, Carbon Fiber Reinforcement, PTFE Lubricant  (discontinued **)&l.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0040 cm/cm
0.0030 - 0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 168 MPa
24400 psi
ASTM D638
Tensile Strength, Yield 177 MPa
25700 psi
ASTM D638
Elongation at Break 1.4 %
1.4 %
ASTM D638
Elongation at Yield 1.4 %
1.4 %
ASTM D638
Tensile Modulus 21.5 GPa
3120 ksi
ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 21.1 GPa
3060 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm

@Thickness 3.18 mm
1.10 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.43 J/cm

@Thickness 3.18 mm
8.30 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 6.30 kJ/m²
3.00 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 31.0 kJ/m²
14.8 ft-lb/in²
ISO 180
Falling Dart Impact 15.1 J
11.1 ft-lb
ASTM D3763
Impact Test 2.97 J
2.19 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic 0.39
0.39
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.34
0.34
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 38.3 x 10-8 mm³/N-M
19.0 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 267 °C
513 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 316 - 321 °C
601 - 610 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi
Copyright © lookpolymers.com All Rights Reserved