LG Chemical SBR 1789 High Acrylonitrile Polymer
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SBR 1789 High Acrylonitrile Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: SSBR 1789 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (RAE type) oil and styrene-butadiene copolymer of 40% bound styrene. Raw materials for this product are carefully chosen for the best physical properties. The aromatic oil in SBR 1789 is an eco-friendly type (RAE) which meets the European legislation on extender oil.Applications: SBR 1789 can be used in tire tread, camelback and other industrial products.CAS No: 9003-55-8Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | |
| Volatiles | 0.20 % | 0.20 % | |
| Mooney Viscosity | 51 @Temperature 100 °C |
51 @Temperature 212 °F |
ML 1+4 |
| Ash | 0.20 % | 0.20 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.7 MPa @Temperature 145 °C, Time 2100 sec |
3580 psi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
| Elongation at Break | 620 % @Temperature 145 °C, Time 2100 sec |
620 % @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
| 300% Modulus | 0.0111 GPa @Temperature 145 °C, Time 2100 sec |
1.61 ksi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Styrene Content | 40 % | 40 % | Bound |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Dark Brown Bale | |
| Components | HAF | 68.75, ASTM D3185 |
| SBR 1739 | 137.5, ASTM D3185 | |
| Stearic Acid | 1, ASTM D3185 | |
| Sulfur | 1.75, ASTM D3185 | |
| TBBS | 1.38, ASTM D3185 | |
| ZnO | 3, ASTM D3185 | |
| Oil Analysis | 0.273 | |
| Organic Acid | 0.05 | |
| Rheometer | 16.8 min | t'90, 160°C, 1° Arc, ASTM D5289 |
| 19.3 lb-in | MH, 160°C, 1° Arc, ASTM D5289 | |
| 3.0 lb-in | ML, 160°C, 1° Arc, ASTM D5289 | |
| 5.2 min | ts1, 160°C, 1° Arc, ASTM D5289 | |
| 9.5 min | t'50, 160°C, 1° Arc, ASTM D5289 | |
| Soap | 0.001 |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PA1501 Polyamide 66 - Carbon Nanotube Masterbatch
- DuPont™ Surlyn® 8120 Ionomer Resin, Sodium (discontinued **)
- Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 10% Plasticizer (discontinued **)
- SABIC Innovative Plastics LNP Thermocomp AF0029 ABS
- Teknor Apex APEX® 90-A471R-75-NT Polyvinyl Chloride, Flexible
- Eastman Tritan TX1800 Copolyester
- Cheng Yu Plastic FV3030 Polyformaldehyde
- Aaron Industries AVPE HD 300-3 MELT 20 Virgin Polyethylene
- BASF Capron® GR20 20% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- BASF Ultraform® N2644 Z9 POM + PUR
Copyright © lookpolymers.com All Rights Reserved