LG Chemical SBR 1723 High Acrylonitrile Polymer
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SBR 1723 High Acrylonitrile Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: SBR 1723 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (PolyCyclic Aromatic) oil and styrene-butadiene copolymer of 23.5% bound styrene. Raw materials for this product are carefully chosen for the best physical properties. The aromatic oil in SBR 1723 is an eco-friendly type (TDAE) which meets the European legislation on extender oil.Applications: SBR 1723 can be used in tire tread, camelback and other industrial products.CAS No: 9003-55-8Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | |
| Volatiles | 0.20 % | 0.20 % | |
| Mooney Viscosity | 49 @Temperature 100 °C |
49 @Temperature 212 °F |
ML 1+4 |
| Ash | 0.10 % | 0.10 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.4 MPa @Temperature 145 °C, Time 2100 sec |
4120 psi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
| Elongation at Break | 600 % @Temperature 145 °C, Time 2100 sec |
600 % @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
| 300% Modulus | 0.0110 GPa @Temperature 145 °C, Time 2100 sec |
1.59 ksi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Styrene Content | 23.5 % | 23.5 % | Bound |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Dark Brown Bale | |
| Components | HAF | 68.75, ASTM D3185 |
| SBR 1723 | 137.5, ASTM D3185 | |
| Stearic Acid | 1, ASTM D3185 | |
| Sulfur | 1.75, ASTM D3185 | |
| TBBS | 1.38, ASTM D3185 | |
| ZnO | 3, ASTM D3185 | |
| Oil Analysis | 0.273 | |
| Organic Acid | 0.05 | |
| Rheometer | 15.1 min | t'90, 160°C, 1° Arc, ASTM D5289 |
| 20.5 lb-in | MH, 160°C, 1° Arc, ASTM D5289 | |
| 3.5 lb-in | ML, 160°C, 1° Arc, ASTM D5289 | |
| 4.2 min | ts1, 160°C, 1° Arc, ASTM D5289 | |
| 9.0 min | t'50, 160°C, 1° Arc, ASTM D5289 | |
| Soap | 0.001 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTech™ PC GR40 Glass Reinforced Polycarbonate
- Precision Polymer Engineering S70S Conductive Silicone Rubber
- Huntsman IROGRAN® A 85 D 4968 Polyester-Based TPU-Injection Extrusion Grade
- Sinotek Materials ZSKP80 Expandable Graphite
- SABIC Innovative Plastics LNP STAT-KON DE0049P PC
- Zeon Chemicals Zetpol® 2020L Hydrogenated Nitrile Elastomomer
- American Polymers API 410 Polystyrene
- Covestro Makrofol® DE 1-1 Polycarbonate
- Arlon 49576R015 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved