LG Chemical LUTENE-H BE0350 HDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | LG Chemical |
| Trade Name | LUTENE-H |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUTENE-H BE0350 HDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUTENE-H BE0350 is an excellent material for blow-molded articles with high density and rigidity. It has good flow characteristics, high parison stability and impact resistance.Applications: Blow molded containers with capacities ranging a few milliliters up to 30litersProcessing Condition: LUTENE-H BE0350 was developed for extrusion blow molding. From 20 to 25 in L/D ratio are suitable for processing. Depending on screw confiation, the cylinders are set to temperatures between 160 and 200°C. The melt temperature can range between 180 and 200°C. The ideal mold temperature should be between 6 and 40°C.Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.958 g/cc | 0.958 g/cc | ASTM D792 |
| Environmental Stress Crack Resistance | 40 hour | 40 hour | F50; ASTM D1693 |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.25 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength, Yield | 29.4 MPa @Thickness 3.20 mm |
4270 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 800 % @Thickness 3.20 mm |
800 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 1.13 GPa | 164 ksi | 15mm/min; ASTM D790 |
| Izod Impact, Notched | 4.41 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
8.27 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.430 W/m-K | 2.98 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 134 °C | 273 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C @Thickness 12.7 mm |
169 °F @Thickness 0.500 in |
ASTM D648 |
| Vicat Softening Point | 130 °C @Load 1.00 kg |
266 °F @Load 2.20 lb |
ASTM D1525 |
Users viewing this material also viewed the following:
- RedEye On Demand PC-ISO for Parts that can be Sterilized
- RheTech Products HP531-01UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black
- PolyOne Edgetek® NL-08GF-02CF/000 Nylon 6/12, Glass/Carbon Fiber Filled (discontinued **)
- Silberline Sparkle Silvex® 793-20-C
- Solvay MIRACARE® TSC 484 Surfactant
- DuPont Bynel® 4164 Anhydride-Modified LLDPE Adhesive Resin
- ChevronTexaco 600 White Oil
- Cytec (Conap) FR-1273 Conapoxy® Resin / Conacure® Hardener
- Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F)
Copyright © lookpolymers.com All Rights Reserved