Jackon JACKOCELL® S214 Expanded Polystyrene Construction and Block Molding

Category Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS)
Manufacturer Jackon GmbH
Trade Name JACKOCELL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Jackon JACKOCELL® S214 Expanded Polystyrene Construction and Block Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Pre-ExpansionThe unique design of polystyrene chains and additive chemistry in Jackocell® S214 gives pre-expanded beads high dimensional stability even at low densities, which typically reduces average operational density, providing a safe road to higher earnings. The S214 represents among the lowest density choices of all Jackocell® EPS grades.Block MouldingIt is different from normal and regular block grades - lower densities in combination with low water absorption and high strength, however at slightly longer moulding times - makes Jackocell® S214 the favorite choice for manufacture of high quality insulation boards. It is best characterized by high heat stability, which gives substantial advantages in block moulding - such as good density control, high strength, good fusion and low scrap to secure financial opportunity losses to the end user.
Physical Properties Metric English Comments
Density 0.0120 g/cc
0.000434 lb/in³
95 second cycle time
0.0145 g/cc
0.000524 lb/in³
73 second cycle time
0.0160 g/cc
0.000578 lb/in³
75 rpm
0.0170 g/cc
0.000614 lb/in³
100 rpm
0.0190 g/cc
0.000686 lb/in³
45 second cycle time
0.0200 g/cc
0.000723 lb/in³
110 second cycle time
0.0200 g/cc
0.000723 lb/in³
125 rpm
Water Absorption 0.80 %
0.80 %
16 g/l; Volume%
0.80 %
0.80 %
18 g/l; Volume%
0.80 %
0.80 %
20 g/l; Volume%
Mechanical Properties Metric English Comments
Flexural Strength 0.120 MPa
17.4 psi
15 g/l
0.200 MPa
29.0 psi
16 g/l
0.230 MPa
33.4 psi
19 g/l
Compressive Strength 0.920 MPa
133 psi
16 g/l
1.07 MPa
155 psi
18 g/l
1.22 MPa
177 psi
20 g/l
Thermal Properties Metric English Comments
Thermal Conductivity 0.0352 W/m-K
0.244 BTU-in/hr-ft²-°F
18 g/l; EN 12667
0.0364 W/m-K
0.253 BTU-in/hr-ft²-°F
16 g/l; EN 12667
0.0384 W/m-K
0.266 BTU-in/hr-ft²-°F
15 g/l; EN 12667
Descriptive Properties Value Comments
Moulding Cycle Time (sec) 190
16 g/l
210
18 g/l
230
20 g/l