Inno-Comp INNOPOL® CS 1-3130 30% Talc-Filled Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-3130 30% Talc-Filled Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-3130 is a 30% talc-filled polypropylene homopolymer compound /PP-H TD30 (ISO 1043)/. This grade is available in natural and custom colored form as well.INNOPOL® CS 1-3130 is recommended especially for producing products, where high stiffness, low shrinkage and long term heat stability are required.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc @Temperature 23.0 °C |
0.0408 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Ash | 28 % @Temperature 900 °C |
28 % @Temperature 1650 °F |
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 3.6 % | 3.6 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 2.70 J/cm² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.210 J/cm² @Temperature -30.0 °C |
0.999 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.280 J/cm² @Temperature 23.0 °C |
1.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 164 °C | 327 °F | DSC; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ISO 75-1,-2 |
| Vicat Softening Point | 153 °C | 307 °F | A120; ISO 306 |
| 192 °C | 378 °F | B120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-81 General Purpose Acrylic Resin
- NanoAmor 95%, OD/ID/L: 10-20/5-10 nm/0.5-2 um Short Multi-Walled Carbon Nanotubes
- Forever Plast Namtene® Recycled Standard HDPE
- Mearthane Durethaneâ„¢ S DS-585DR Solid Polyurethane Elastomer
- SABIC Innovative Plastics Valox® 337 PBT
- Techmer ES HiFill® ABS GF30 30% Glass Filled
- Sharadaa Ceramics REFINSUL ZAP-014 Insulating Castables
- Elektro-Isola Etronax MFP G Phenolic, Cotton Fabric Reinforcement, Black, Tubes
- DuPont Performance Polymers Zytel® 45HSB NC010 Nylon 66 (Unverified Data**)
- Amity Thermosets ATS 751 Phenolic Molding Inorganic and glass fiber Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved