Ineos N20L-00 Polypropylene Impact Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos N20L-00 Polypropylene Impact Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a nucleated polypropylene impact copolymer formulated with a slip agent for improved mold release, and has an optimum balance of stiffness and impact resistance for injection molding applications. It is particularly well suited for Material Handling applications such as crates for food transport and storage. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsConsumer productsMaterial handling productsIndustrial applicationsBenefitsGood impact to stiffness balanceLubricated for improved mold releaseInformation provided by Ineos Olefins & Polymers USA
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 61 | 61 | ASTM D785 |
| Tensile Strength, Yield | 21.1 MPa @Temperature 23.0 °C |
3060 psi @Temperature 73.4 °F |
ASTM D638 |
| Elongation at Yield | 5.4 % | 5.4 % | ASTM D638 |
| Flexural Modulus, 1% Secant | 979 MPa @Temperature 23.0 °C |
142000 psi @Temperature 73.4 °F |
0.05 in/min test speed |
| Izod Impact, Notched | 1.44 J/cm @Temperature -20.0 °C |
2.70 ft-lb/in @Temperature -4.00 °F |
1/8'' notched bar; ASTM D256 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
1/8'' notched bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.7 °C | 188 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Instrumented Impact (Dynatup) | Ductile | 23°C, D3763 |
| Ductile | negative 20°C, D3763 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL® 6308 Conductive Elastomer
- MarkeTech Cu/Mo/Cu 1:5:1 Laminated Sheet
- SABIC Innovative Plastics LNP Thermocomp WF007 PET/PBT
- Styron XZ 91982.00 Carboxylated SB
- A. Schulman POLYBATCH™ Beige 6027E Concentrate Based In Polyethylene
- Eagle Brass 260 Cartridge Brass, 1/4 Hard
- Carmel Olefins CAPILENE® HT 75 A Polypropylene Impact Copolymer
- ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, 1149°C (2100°F) Solution Treated, UNS N06601
- BASF Ultradur B 4300 G4 LS High Speed BK15045 20% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved