Ineos N00N-00 Polypropylene Impact Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Ineos N00N-00 Polypropylene Impact Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Grade N00N-00 is a fractional melt flow rate, high impact copolymer polypropylene specifically designed for non-pressure structured wall pipe but can also be used in other extrusion applications requiring high melt strength and high stiffness. It offers a superior balance of stiffness and impact strength as compared to competitive impact copolymers of similar melt flow rate.Applications:Non-pressure pipe and fittingsSheet extrusionBlow moldingBenefits and Features:Very high stiffnessGood impact resistanceHigh melt strengthVery good long term stabilityInformation provided by Ineos Olefins & Polymers USA
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Oxidative Induction Time (OIT) | >= 70 min <br>@Temperature 200 °C |
>= 70 min <br>@Temperature 392 °F |
ASTM 3895 |
| Melt Flow | 0.35 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
0.35 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | ASTM D638 |
| Elongation at Yield | >= 8.5 % | >= 8.5 % | ASTM D638 |
| Flexural Modulus | 1.29 GPa | 187 ksi | 2% Secant, Injection Molded Sample, 0.05 in/min test speed; ASTM D790 |
| 1.45 GPa | 211 ksi | 1% Secant, Injection Molded Sample, 0.05 in/min test speed; ASTM D790 | |
| 1.54 GPa | 223 ksi | Tangent, Injection Molded Sample, 0.05 in/min test speed; ASTM D790 | |
| Izod Impact, Notched | 1.01 J/cm <br>@Temperature -20.0 °C |
1.90 ft-lb/in <br>@Temperature -4.00 °F |
ASTM D256 |
| NB <br>@Temperature 23.0 °C |
NB <br>@Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM D256 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Blow Molding | |
| Pipe Extrusion | ||
| Sheet Extrusion | ||
| Region | Mexico | Bamberger Polymers Distribution |
| US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D-5016
- Rogers Corporation RO4534 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate
- PolyOne Geon™ Vinyl Fittings M1012 Polyvinyl Chloride, Rigid (PVC, Rigid)
- ITW Devcon Flexane® Rubber Repair / Castable Urethane 80 Putty, Black
- Karina E 85/253-IS-SI-AT Compound PVC Crystal
- Solvay Specialty Polymers Amodel® A-4145 HH Polyphthalamide (PPA), 45% Glass Fiber (Conditioned)
- Sharadaa Ceramics HA 62D High Alumina Brick
- Solvay RHODOLINE® 681-F Surfactant
- Ascend Performance Materials Vydyne® 49 Nylon 66, DAM
- A. Schulman ComAlloy Hiloy® 419 Polyester - PBT, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved