Industrial Laminates/Norplex NP612 Paper Base Laminate

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP612 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Room temperature punching and shearing grade up to .125" thick. More flexible and lower mechanical properties than NP611. Intended for applications where electrical and moisture requirements are secondary.Thickness Tested: 0.062", 0 125" and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.35 - 1.40 g/cc

@Thickness 1.57 mm
 1.35 - 1.40 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 3.2 %

@Thickness 1.57 mm
 3.2 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 65 - 85

@Thickness 1.57 mm
 65 - 85

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 57.9 MPa

@Thickness 1.57 mm
 8400 psi

@Thickness 0.0620 in
 CW; ASTM D638
86.2 MPa

@Thickness 1.57 mm
 12500 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 5.86 GPa

@Thickness 1.57 mm
 850 ksi

@Thickness 0.0620 in
 CW; ASTM D229
6.89 GPa

@Thickness 1.57 mm
 1000 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 121 MPa

@Thickness 1.57 mm
 17600 psi

@Thickness 0.0620 in
 CW; ASTM D790
131 MPa

@Thickness 1.57 mm
 19000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 186 MPa

@Thickness 12.7 mm
 27000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 65.5 MPa

@Thickness 15.7 mm
 9500 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.352 J/cm

@Thickness 12.7 mm
 0.660 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
0.406 J/cm

@Thickness 12.7 mm
 0.760 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 19.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 10.6 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 15.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.33 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 5.5

@Thickness 1.57 mm
 5.5

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 27.6 kV/mm

@Thickness 1.57 mm
 700 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 55000 V

@Thickness 1.57 mm
 55000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.060

@Thickness 1.57 mm
 0.060

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 110 sec

@Thickness 3.17 mm
 110 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 500 V

@Thickness 3.17 mm
 500 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1400 lb
0.5", ASTM D229
Color Natural, Black