Industeel CLC 1.2316S Prehardened Mold Steel (300HB) with Improved Machinability
| Category | Metal , Ferrous Metal , Tool Steel , Mold Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | CLC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel CLC 1.2316S Prehardened Mold Steel (300HB) with Improved Machinability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLC 1.2316 S grade is a 16%Cr 1%Mo mold steel with improved corrosion resistance properties, thanks to the chromium and molybdenum additions. Furthermore specific sulfur additions are considered to increase the machinability properties. The grade in the quenched tempered condition has a fully bainite martensite microstructure and can be delivered in the prehardened condition (300HB or 340HB). The grade is not designed for highly finish polished surfaces or etched surfaces. The grade is commonly used for mold steel applications including cores, inserts, molds… subjected to wet working conditions and / or storage conditions. The grade is also used for the manufacturing of corrosive materials like PVC.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.75 g/cc | 0.280 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 340 | 340 | Typical, in Longitudinal |
| Tensile Strength, Ultimate | 1160 MPa | 168000 psi | Typical, Longitudinal Direction |
| Tensile Strength, Yield | 950 MPa @Strain 0.200 % |
138000 psi @Strain 0.200 % |
Typical, Longitudinal Direction |
| Elongation at Break | 10 % | 10 % | Typical, EL 5.65 Longitudinal Direction |
| Modulus of Elasticity | 207 GPa | 30000 ksi | Typical, in Longitudinal Direction |
| Charpy Impact | 12.0 J | 8.85 ft-lb | Typical (Longitudinal) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 100 °C |
6.11 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 11.1 µm/m-°C @Temperature 20.0 - 200 °C |
6.17 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 11.7 µm/m-°C @Temperature 20.0 - 400 °C |
6.50 µin/in-°F @Temperature 68.0 - 752 °F |
||
| Specific Heat Capacity | 0.460 J/g-°C @Temperature 20.0 °C |
0.110 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 24.3 W/m-K @Temperature 20.0 °C |
169 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.40 % | 0.40 % | |
| Chromium, Cr | 16 % | 16 % | |
| Iron, Fe | 81.32 - 81.42 % | 81.32 - 81.42 % | As remainder |
| Manganese, Mn | 0.80 % | 0.80 % | |
| Molybdenum, Mo | 1.03 % | 1.03 % | |
| Phosphorous, P | <= 0.030 % | <= 0.030 % | |
| Silicon, Si | 0.35 % | 0.35 % | |
| Sulfur, S | <= 0.070 % | <= 0.070 % |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S80H Silicone Rubber
- Gharda Chemicals Gafone™ T6500 Polysupersulfone (PSS) (discontinued **)
- ICO Polymers ICOFLOâ„¢ 510-5069 400 Micron LLDPE Powder
- Indium Corp. 16-2212 Flux Thinner
- A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
- Arlon Thermabond® 48781A008 0.008" (0.203 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M Scotch-Weld™ MG100 LO Medical Grade Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved