ICO Polymers ICOFLOâ„¢ 510-5053 500 Micron LDPE Powder
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Masterbatch Grade |
| Manufacturer | ICO Polymers (A Schulman Inc.) |
| Trade Name | ICOFLO™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ICO Polymers ICOFLOâ„¢ 510-5053 500 Micron LDPE Powder.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ICOFLO 510-5053 is a premium polyethylene powder specifically designed to be used in the preparation of masterbatch (concentrate). By utilizing a free flowing powder as a carrier in masterbatch (instead of pellet), superior color development or additive dispersion can be achieved in the final concentrate. Key Characteristics: good stiffness, good impact strength and excellent appearance. Information provided by ICO Polymers.A Schulman acquired ICO, Inc. in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Particle Size | >= 150 µm | >= 150 µm | pan, 13% |
| <= 500 µm | <= 500 µm | sieve < 5% | |
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.200 GPa | 29.0 ksi | 1 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 111 °C | 232 °F | DSC; ASTM D3418 |
| Vicat Softening Point | 82.0 °C | 180 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | recommended |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Max Dry Flow | max 31 sec/100g | ASTM |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL6414 PC (Asia Pacific)
- Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F)
- Henkel Frekote PMC Mold Solvent
- Solvay Chemicals Perstabil
- SABIC Innovative Plastics LNP Thermocomp DF002L PC
- Trelleborg Fillite® 160W Alumino-silicate Cenospheres
- Arlon P29514R020P 0.0205" (0.521 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate
- BASF Ultramid® B35EG3 15% Glass Filled PA6 (Conditioned)
- Compuestos Dominicanos Polycom CO-160355 PVC Compound
- H.C. Starck Amperit® 335.066 Nickel Self-fluxing Alloy HRC 60 (NiCrBSi)
Copyright © lookpolymers.com All Rights Reserved