Hybrid Plastics FireQuench® PM 1287 Resin
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset |
| Manufacturer | Hybrid Plastics |
| Trade Name | FireQuench® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hybrid Plastics FireQuench® PM 1287 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FireQuench® PM1287 is an optically transparent, fire retardant hybrid nanocomposite resin that can serve as a replacement for standard epoxy-vinyl ester and related resins. It can be employed as an unfilled, nanocomposite resin or it can be filled and utilized with reinforcements such as glass fiber. FireQuench® PM1287 has significantly improved thermal and flame retardant properties when compared to all other high temperature thermoset resins.Information provided by Hybrid Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Viscosity | 100 cP | 100 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | 1.7 % | 1.7 % | composite |
| 3.5 % | 3.5 % | resin | |
| Flexural Strength | 93.169 MPa @Temperature 23.0 °C |
13513 psi @Temperature 73.4 °F |
resin |
| 463 MPa @Temperature 23.0 °C |
67200 psi @Temperature 73.4 °F |
composite | |
| Flexural Modulus | 0.965 GPa @Temperature 23.0 °C |
140 ksi @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat Distortion Temperature | <= 600 °C | <= 1110 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Gel Time | 45.0 - 60.0 min @Temperature 60.0 °C |
45.0 - 60.0 min @Temperature 140 °F |
with 0.2%wt catalyst load |
| Shelf Life | 24.0 - 36.0 Month | 24.0 - 36.0 Month | w/o catalyst |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LGN2000 PC (Asia Pacific)
- PolyOne Maxxam™ FR PP 301 Black 1284-11 S Polypropylene, Unspecified (PP, Unspecified)
- NOVA Chemicals Sclair® 2508-UV9 MDPE Injection Molding Resin (discontinued **)
- Glastic Laminates/Shapes 2165 Fiberglass-Reinforced Polyester Standoff Insulator
- Lubrizol Advanced Materials PEARLBOND® 122 Linear Thermoplastic Polyurethane
- Karina E 75800-35/1-B-AC Ivory PVC Compound
- Skamol Group Moler BB-Filler Aggregate Insulation
- Carlson Nitronic® 60® Austenitic Stainless Steel
- BASF Ultramid® 8266G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry)
- DSM Arnite® T06 206 T Impact Modified PBT (European Grade) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved