- Huntsman KRYSTALFLEX® PE 193 Polyurethane Optical Aliphatic Film
Huntsman KRYSTALFLEX® PE 193 Polyurethane Optical Aliphatic Film
| Category | Polymer , Film , Thermoplastic , Polyurethane, TP |
| Manufacturer | Huntsman Corporation |
| Trade Name | KRYSTALFLEX® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman KRYSTALFLEX® PE 193 Polyurethane Optical Aliphatic Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Properties:Moisture ResistanceChemical CompatibilityCooler ProcessingHigher AdhesionMultiple Design OptionNo special storage requiredInformation provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 74 | 74 | ASTM D2240 |
| Tensile Strength at Break | 20.7 MPa | 3000 psi | ASTM D412 |
| Elongation at Break | 600 % | 600 % | ASTM D412 |
| 100% Modulus | 0.00276 GPa | 0.400 ksi | ASTM D412 |
| 300% Modulus | 0.00552 GPa | 0.800 ksi | ASTM D412 |
| Tear Strength | 64.9 kN/m | 370 pli | ASTM D624 |
| Peel Strength | 24.0 kN/m @Temperature 99.0 °C |
137 pli @Temperature 210 °F |
resistance to glass with primer; ASTM D3167 |
| 26.3 kN/m @Temperature 113 °C |
150 pli @Temperature 235 °F |
resistance to glass with primer; ASTM D3167 | |
| 28.0 kN/m @Temperature 127 °C |
160 pli @Temperature 261 °F |
resistance to glass with primer; ASTM D3167 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -44.0 °C | -47.2 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 85.0 - 120 °C | 185 - 248 °F |
Users viewing this material also viewed the following:
- Polimeri Europa Edistir RT 461F Polystyrene
- LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced
- Lehmann & Voss LUVOCOM® 1105/GF/14 PEEK, with glass fiber
- Solvay Chemicals NOCOLOK® Li Flux Drystatic
- Spartech PP7220 Calcium Carbonate Filled High Impact Copolymer
- Saint-Gobain CHR® M887 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- Master Bond Mastersil 410 One Component Room Temperature Curing Silicon
- Terio Corporation TZY-4 Yttria Stabilized Zirconia
- A. Schulman POLYBATCH™ Red 502 Concentrate Based In Polyethylene
- A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound
Copyright © lookpolymers.com All Rights Reserved