Huntsman IROGRAN® A 85 D 5001 Polyester-Based TPU-Injection Extrusion Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 85 D 5001 Polyester-Based TPU-Injection Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Hydrolysis resistance and good crystallinity. Suggested for extrusion.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| Hardness, Shore D | 35 | 35 | ASTM D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | DIN 53504 |
| Elongation at Break | 800 % | 800 % | ASTM D412 |
| 100% Modulus | 0.00550 GPa | 0.798 ksi | DIN 53504 |
| 300% Modulus | 0.0126 GPa | 1.83 ksi | DIN 53504 |
| Rebound | 36 % | 36 % | Bayshore; ASTM D2632 |
| Tear Strength | 105 kN/m | 600 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 19 % @Temperature 23.0 °C, Time 252000 sec |
19 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 36 % @Temperature 70.0 °C, Time 86400 sec |
36 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 175 °C | 329 - 347 °F | Huntsman/TMA |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 5.00e+8 ohm | 5.00e+8 ohm | antistat |
Users viewing this material also viewed the following:
- MV Labs PT165 Na2Pt(CN)4.3H2O Sodium tetracyanoplatinate(II) hydrate
- Parker Chomerics CHO-SEAL® 6452 Conductive Elastomer
- Ferro EG 0002 Glazes and Sealants
- A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene
- DSM Akulon® K224-PG2 PA6-I-GF8
- Eurotec® Tecotek® PC43 GR30 BK002 PC, 30% glass fiber reinforced, black
- BASF tert.-Butylamine
- ATI Allegheny Ludlum Type AL 441HP™ Stainless Steel Alloy
- Teknor Apex Chemlon® 214 GH Nylon 6, 14% Short Glass Fiber
Copyright © lookpolymers.com All Rights Reserved