- Honeywell ACLAR® CX 130E Heat Sealable PCTFE Film (discontinued **)
Honeywell ACLAR® CX 130E Heat Sealable PCTFE Film (discontinued **)
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® CX 130E Heat Sealable PCTFE Film
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® CX 130E is a heat sealable PCTFE film with outstanding clarity. It is used where applications require moisture protection.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D1505 |
| Density | 1.22 g/cc | 0.0440 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.0780 g/m²/day | 0.00502 g/100 in²/day | 77°F (25°C) / 60%RH; ASTM F1249 |
| 0.155 g/m²/day | 0.00998 g/100 in²/day | 86°F (30°C) / 60%RH; ASTM F1249 | |
| 0.510 g/m²/day | 0.0328 g/100 in²/day | 104°F (40°C) / 75%RH; ASTM F1249 | |
| 0.780 g/m²/day | 0.0502 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 | |
| Oxygen Transmission Rate | 202 - 233 cc/m²/day | 13.0 - 15.0 cc/100 in²/day | 25°C / 0%RH; ASTM D3985 |
| Thickness | 33.0 microns | 1.30 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 17.9 - 20.0 MPa | 2600 - 2900 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.9 - 20.0 MPa | 2600 - 2900 psi | ASTM D882 |
| Film Elongation at Break, MD | 75 - 100 % | 75 - 100 % | ASTM D882 |
| Film Elongation at Break, TD | 225 - 325 % | 225 - 325 % | ASTM D882 |
| Film Elongation at Yield, MD | 7.0 - 9.0 % | 7.0 - 9.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 7.0 - 9.0 % | 7.0 - 9.0 % | ASTM D882 |
| Secant Modulus, MD | 0.448 - 0.586 GPa | 65.0 - 85.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.448 - 0.586 GPa | 65.0 - 85.0 ksi | ASTM D882 |
| Falling Dart Impact | 0.813 - 1.08 J | 0.600 - 0.800 ft-lb | ASTM D4272 |
| Coefficient of Friction | 0.40 - 0.60 | 0.40 - 0.60 | Aclar® to metal; ASTM D1894 |
| Coefficient of Friction, Static | 0.60 - 0.80 | 0.60 - 0.80 | Aclar® to metal; ASTM D1894 |
| Tear Strength Test | 350 - 375 | 350 - 375 | graves tear MD, grams/mil; ASTM D1004 |
| 350 - 375 | 350 - 375 | graves tear TD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 26.2 - 31.7 MPa | 3800 - 4600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.9 - 20.0 MPa | 2600 - 2900 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D1003 |
| Gloss | 130 - 140 % | 130 - 140 % | at 20°; ASTM D523 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Interlayer Bond Strength | min 450 g/in | ASTM F904 |
| Puncture Strength | 250-300 g | ASTM F1309 |
Users viewing this material also viewed the following:
- RheTech Products M25UVP250-01 25% Mica Reinforced Polypropylene Copolymer, UV Stabilized, Black
- Ravago Manufacturing Americas Hylex® P1025G10 HB Polycarbonate, 10% Glass Reinforced
- Multibase Multi-Flex® A 8502 LC UV RXF/YYWA Black TPE Thermoplastic Elastomer
- Shinil Chemical SHINFLAME PA-6 GF Flame Retardant Polymer Parts
- A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Clariant Renol BR2084 Nylon 66, 33% Glass Fiber, PTFE Lubricated
- ALIMEX PLANAL 7075 T651/T652 Aluminum Alloy
- Buckeye Polymers BP RPP 2006 T Polypropylene, 20% Mineral Filled
- Addiplast Addinyl C2 Nylon 66/6
- Samyang Trirex® 3020R Polycarbonate with Heat Stabilizer
Copyright © lookpolymers.com All Rights Reserved