Hexcel® Redux® 810 Two-Part Epoxy Paste Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Hexcel
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® Redux® 810 Two-Part Epoxy Paste Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Redux® 810 is a multi-purpose, high shear and peel strength, two-part, toughened epoxy paste adhesive with corrosion-inhibiting properties.Features: Available in cartridges with a static mixer and in tins; Easy to mix; Excellent high shear strength and very high peel properties; Corrosion-inhibiting; Toughened; Non-slump characteristic to 3mm thickness; Gap filling; Glue line control; Service temperature up to 100°C/212°F.Applications: Metal, honeycomb and fibre-reinforced composite bonding applications; Structural repair; Bonding inserts and ferrules; Bonding aluminum and composite edge members; Fabrication of honeycomb sandwich panels using the cut and fold technique.
Physical Properties Metric English Comments
Density 1.02 g/cc
<br>@Temperature 25.0 °C
 0.0368 lb/in³
<br>@Temperature 77.0 °F
 Part B; ASTM D1622
1.11 g/cc
<br>@Temperature 25.0 °C
 0.0401 lb/in³
<br>@Temperature 77.0 °F
 Mixed; ASTM D1622
1.15 g/cc
<br>@Temperature 25.0 °C
 0.0415 lb/in³
<br>@Temperature 77.0 °F
 Part A; ASTM D1622
Viscosity 4000 - 8000 cP
<br>@Temperature 25.0 °C
 4000 - 8000 cP
<br>@Temperature 77.0 °F
 Part B; 0.50mm Gap, 40mm Parallel Plate, Strain = 0.01%; Bohlin Rheometer
80000 - 90000 cP
<br>@Temperature 25.0 °C
 80000 - 90000 cP
<br>@Temperature 77.0 °F
 Part A; 0.50mm Gap, 40mm Parallel Plate, Strain = 0.01%; Bohlin Rheometer
80000 - 100000 cP
<br>@Temperature 25.0 °C
 80000 - 100000 cP
<br>@Temperature 77.0 °F
 Mixed; 0.50mm Gap, 40mm Parallel Plate, Strain = 0.01%; Bohlin Rheometer
Mechanical Properties Metric English Comments
Hardness, Shore D 77
<br>@Temperature 22.2 °C
 77
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 5 days @ 22°C/72°F, Conditioning: Dry; ISO R868
79
<br>@Temperature 22.2 °C
 79
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 1 hour @ 70°C/158°F, Conditioning: Dry; ISO R868
Tensile Strength, Yield 7.398 MPa
<br>@Temperature 22.2 °C
 1073 psi
<br>@Temperature 72.0 °F
 Flatwise Tensile, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-4
8.398 MPa
<br>@Temperature 22.2 °C
 1218 psi
<br>@Temperature 72.0 °F
 Flatwise Tensile, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-4
27.50 MPa
<br>@Temperature 22.2 °C
 3988 psi
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 5 days @ 22°C/72°F, Conditioning: Dry; ISO R527
40.00 MPa
<br>@Temperature 22.2 °C
 5802 psi
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 1 hour @ 70°C/158°F, Conditioning: Dry; ISO R527
Elongation at Break 2.47 %
<br>@Temperature 22.2 °C
 2.47 %
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 5 days @ 22°C/72°F, Conditioning: Dry; ISO R527
5.53 %
<br>@Temperature 22.2 °C
 5.53 %
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 1 hour @ 70°C/158°F, Conditioning: Dry; ISO R527
Tensile Modulus 1.73 GPa
<br>@Temperature 72.0 °C
 251 ksi
<br>@Temperature 162 °F
 Cured Neat Resin Property, 1 hour @ 70°C/158°F, Conditioning: Dry; ISO R527
2.01 GPa
<br>@Temperature 72.0 °C
 291 ksi
<br>@Temperature 162 °F
 Cured Neat Resin Property, 5 days @ 22°C/72°F, Conditioning: Dry; ISO R527
Compressive Yield Strength 10.0 MPa
<br>@Temperature 60.0 °C
 1450 psi
<br>@Temperature 140 °F
 Cured Neat Resin Property, 1 hour @ 70°C/158°F, Conditioning: Dry; ASTM D695
10.0 MPa
<br>@Temperature 60.0 °C
 1450 psi
<br>@Temperature 140 °F
 Cured Neat Resin Property, 5 days @ 22°C/72°F, Conditioning: Dry; ASTM D695
35.50 MPa
<br>@Temperature 22.2 °C
 5149 psi
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 1 hour @ 70°C/158°F, Conditioning: Dry; ASTM D695
47.50 MPa
<br>@Temperature 22.2 °C
 6889 psi
<br>@Temperature 72.0 °F
 Cured Neat Resin Property, 5 days @ 22°C/72°F, Conditioning: Dry; ASTM D695
Poissons Ratio 0.53
0.53
Cured Neat Resin Property, 1 hour @ 70°C/158°F, Conditioning: Dry
0.68
0.68
Cured Neat Resin Property, 5 days @ 22°C/72°F, Conditioning: Dry
Shear Strength 6.902 MPa
<br>@Temperature 100 °C
 1001 psi
<br>@Temperature 212 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-1
11.20 MPa
<br>@Temperature 100 °C
 1624 psi
<br>@Temperature 212 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-1
16.2 MPa
<br>@Temperature 80.0 °C
 2350 psi
<br>@Temperature 176 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-1
16.30 MPa
<br>@Temperature 40.0 °C
 2364 psi
<br>@Temperature 104 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: 60°C / 140°F - 95% RH - 30 Days; EN2243-1
17.50 MPa
<br>@Temperature 40.0 °C
 2538 psi
<br>@Temperature 104 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: 60°C / 140°F - 95% RH - 30 Days; EN2243-1
22.80 MPa
<br>@Temperature 60.0 °C
 3307 psi
<br>@Temperature 140 °F
 Tensile Lap Shear, 1 hour @ 120°C/248°F, Conditioning: Dry; EN2243-1
23.90 MPa
<br>@Temperature -55.0 °C
 3466 psi
<br>@Temperature -67.0 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-1
24.00 MPa
<br>@Temperature 80.0 °C
 3481 psi
<br>@Temperature 176 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-1
25.80 MPa
<br>@Temperature 60.0 °C
 3742 psi
<br>@Temperature 140 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-1
29.68 MPa
<br>@Temperature 60.0 °C
 4305 psi
<br>@Temperature 140 °F
 Tensile Lap Shear, 1 hour @ 100°C/212°F, Conditioning: Dry; EN2243-1
33.90 MPa
<br>@Temperature 22.2 °C
 4917 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: 60°C / 140°F - 95% RH - 30 Days; EN2243-1
35.3 MPa
<br>@Temperature 22.2 °C
 5120 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: Salt Spray 2000 hours; EN2243-1
35.50 MPa
<br>@Temperature 22.2 °C
 5149 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: Salt Spray 2000 hours; EN2243-1
35.60 MPa
<br>@Temperature 22.2 °C
 5163 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: 60°C / 140°F - 95% RH - 30 Days; EN2243-1
37.80 MPa
<br>@Temperature 60.0 °C
 5482 psi
<br>@Temperature 140 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-1
38.10 MPa
<br>@Temperature 22.2 °C
 5526 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 1 hour @ 120°C/248°F, Conditioning: Dry; EN2243-1
41.3 MPa
<br>@Temperature 22.2 °C
 5990 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-1
43.3 MPa
<br>@Temperature 22.2 °C
 6280 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 1 hour @ 100°C/212°F, Conditioning: Dry; EN2243-1
46.60 MPa
<br>@Temperature 22.2 °C
 6759 psi
<br>@Temperature 72.0 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-1
48.90 MPa
<br>@Temperature -55.0 °C
 7092 psi
<br>@Temperature -67.0 °F
 Tensile Lap Shear, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-1
Peel Strength 1.40 kN/m
<br>@Temperature 100 °C
 8.00 pli
<br>@Temperature 212 °F
 Bell Peel, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-2
1.58 kN/m
<br>@Temperature 100 °C
 9.00 pli
<br>@Temperature 212 °F
 Bell Peel, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-2
5.08 kN/m
<br>@Temperature 80.0 °C
 29.0 pli
<br>@Temperature 176 °F
 Bell Peel, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-2
5.61 kN/m
<br>@Temperature 80.0 °C
 32.0 pli
<br>@Temperature 176 °F
 Bell Peel, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-2
8.41 kN/m
<br>@Temperature 60.0 °C
 48.0 pli
<br>@Temperature 140 °F
 Bell Peel, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-2
9.29 kN/m
<br>@Temperature 22.2 °C
 53.0 pli
<br>@Temperature 72.0 °F
 Bell Peel, 1 hour @ 70°C/158°F, Conditioning: Dry; EN2243-2
12.4 kN/m
<br>@Temperature 60.0 °C
 71.0 pli
<br>@Temperature 140 °F
 Bell Peel, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-2
13.1 kN/m
<br>@Temperature 22.2 °C
 75.0 pli
<br>@Temperature 72.0 °F
 Bell Peel, 5 days @ 22°C/72°F, Conditioning: Dry; EN2243-2
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 42.8 °C
109 °F
Tg onset, 60°C/140°F-95%RH, 30days; Cured Neat Resin Property, 5 days @ 22°C/72°F
43.9 °C
111 °F
Tg onset, 60°C/140°F-95%RH, 30days; Cured Neat Resin Property, 1 hour @ 70°C/158°F
52.8 °C
127 °F
Tg tan d, 60°C/140°F-95%RH, 30days; Cured Neat Resin Property, 5 days @ 22°C/72°F
53.9 °C
129 °F
Tg tan d, 60°C/140°F-95%RH, 30days; Cured Neat Resin Property, 1 hour @ 70°C/158°F
58.9 °C
138 °F
Tg onset, Dry, Cured Neat Resin Property, 5 days @ 22°C/72°F
70.0 °C
158 °F
Tg tan d, Dry, Cured Neat Resin Property, 5 days @ 22°C/72°F
72.2 °C
162 °F
Tg onset, Dry, Cured Neat Resin Property, 1 hour @ 70°C/158°F
88.9 °C
192 °F
Tg tan d, Dry, Cured Neat Resin Property, 1 hour @ 70°C/158°F
Processing Properties Metric English Comments
Cure Time 2.00 min
<br>@Temperature 120 °C
 0.0333 hour
<br>@Temperature 248 °F
 EN 2243-1
5.00 min
<br>@Temperature 100 °C
 0.0833 hour
<br>@Temperature 212 °F
 EN 2243-1
20.0 min
<br>@Temperature 70.0 °C
 0.333 hour
<br>@Temperature 158 °F
 EN 2243-1
300 min
<br>@Temperature 40.0 °C
 5.00 hour
<br>@Temperature 104 °F
 EN 2243-1
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved