Hexcel® HexWeb® HRH-310 - 1/8 - 1.8 Aramid Fiber/Polyimide Resin Honeycomb

Category Other Engineering Material , Composite Fibers , Polymer , Thermoset , Aramid , Polyimide, TS
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-310 - 1/8 - 1.8 Aramid Fiber/Polyimide Resin Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size-DensityHexWeb HRH-310 is manufactured from aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal confiation, the block is dipped in polyimide resin. After curing the resin, slices are cut to the desired thickness. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced. An OX-Core confiation featuring enhanced formability is available upon special request.Features: Outstanding dielectric and loss tangent properties; Small cell sizes at low densities; Relatively damage resistant; Formability; Good bonding surfaces; Good thermal and electrical insulator.Applications: Outstanding results have been reported with the use of HexWeb HRH-310 in a sandwich structure as both a strip antenna and a radome. Although a polyimide resin is used, HexWeb HRH-310 is not recommended for high-temperature applications. The polyimide resin is used for electrical reasons only.
Physical Properties Metric English Comments
Density 0.0288 g/cc
0.00104 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 0.359 MPa
>= 52.0 psi
Bare, minimum individual
>= 0.379 MPa
>= 55.0 psi
Bare, minimum avg
Shear Modulus >= 0.00689 GPa
>= 1.00 ksi
Plate Shear, W Direction, minimum individual
>= 0.00758 GPa
>= 1.10 ksi
Plate Shear, w Direction, minimum avg.
>= 0.0207 GPa
>= 3.00 ksi
Plate Shear, L Direction, minimum individual
>= 0.0228 GPa
>= 3.30 ksi
Plate Shear, L Direction, minimum avg.
Shear Strength >= 0.159 MPa
>= 23.0 psi
Plate Shear, W Direction, minimum avg.
>= 0.172 MPa
>= 25.0 psi
Plate Shear, W Direction, minimum avg.
>= 0.345 MPa
>= 50.0 psi
Plate Shear, L Direction, minimum individual
>= 0.359 MPa
>= 52.0 psi
Plate Shear, L Direction, minimum avg.