Hexcel® HexWeb® HRH-10/OX - 3/16 - 1.8 Aramid Fiber/Phenolic Resin Honeycomb

Category Other Engineering Material , Composite Core Material , Composite Fibers , Polymer , Thermoset , Aramid , Phenolic
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-10/OX - 3/16 - 1.8 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core confiation, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.0288 g/cc
0.00104 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 0.586 MPa
>= 85.0 psi
Bare, min
>= 0.655 MPa
>= 95.0 psi
Stabilized, min
0.758 MPa
110 psi
Bare, typ
0.827 MPa
120 psi
Stabilized, typ
Compressive Modulus 0.0483 GPa
7.00 ksi
Stabilized, typ
Shear Modulus 0.0138 GPa
2.00 ksi
Plate Shear, L Direction, typ
0.0207 GPa
3.00 ksi
Plate Shear, W Direction, typ
Shear Strength >= 0.310 MPa
>= 45.0 psi
Plate Shear, L Direction, min
>= 0.345 MPa
>= 50.0 psi
Plate Shear, W Direction, min
0.448 MPa
65.0 psi
Plate Shear, L Direction, typ
0.483 MPa
70.0 psi
Plate Shear, W Direction, typ